Laminated glass
View Patent ↗There is provided a laminated glass that has both of a rigidity and a sound insulating property while attaining the weight reduction. The laminated glass comprises a pair of glass plates each having a plate thickness of 0.3 mm to 1.8 mm; and an interlayer film provided between the glass plates and having a storage elastic modulus G′ equal to or greater than 2.0×10 6 Pa at a frequency of 1 Hz and temperature of 20° C., wherein the laminated glass has a loss factor equal to or greater than 0.2 at one or more resonance points at the frequency of 3 to 6 KHz and the temperature of 20° C.
1. A laminated glass, comprising:
a pair of glass plates each having a plate thickness of 0.3 mm to 1.8 mm; and
an interlayer film provided between the glass plates and having a storage elastic modulus G′ equal to or greater than 2.0×10 6 Pa at a frequency of 1 Hz and temperature of 20° C.,
wherein the laminated glass has a loss factor equal to or greater than 0.2 at one or more resonance points at the frequency of 3 to 6 KHz and the temperature of 20° C.
the interlayer film of the laminated glass is composed of three layer including a core layer and a pair of outer layers configured to sandwich the core layer,
a storage elastic modulus G's of the outer layers are equal to or greater than 5.0×10 6 Pa and equal to or less than 1.3×10 8 Pa at the frequency of 1 Hz and the temperature of 20° C.,
a storage elastic modulus G′ of the core layer is equal to or greater than 1.0×10 4 Pa and equal to or less than 1.0×10 7 Pa at the frequency of 1 Hz and the temperature of 20° C.,
the core layer has a smaller storage elastic modulus G′ at the frequency of 1 Hz and the temperature of 20° C. compared to the pair of the outer layers, and,
a layer thickness of the core layer is 0.05 mm to 0.30 mm.
2. The laminated glass according to claim 1 , wherein the pair of glass plates have different thickness each other.
3. The laminated glass according to claim 1 , wherein the core layer has a glass transition point within a range of 0° C. to 20° C.
4. The laminated glass according to claim 1 , wherein the laminated glass is usable as a side glass, a roof glass, or a rear glass for a vehicle.
5. The laminated glass according to claim 1 , wherein the laminated glass has a rigidity measured by a three point bend test is equal to or greater than 100 N/mm.
6. The laminated glass according to claim 1 , wherein the laminated glass has a sound transmission loss equal to or greater than 25 dB measured at the temperature of 20° C. in compliance with SAE J1400.
7. The laminated glass according to claim 1 , wherein a proportional value of the storage elastic modulus G's of the outer layers with respect to the storage elastic modulus G′ of the core layer is 100 to 3000.
8. The laminated glass according to claim 1 , wherein the laminated glass is usable as a side glass for a vehicle.