Copolymer fibers and yarns and processes for making same
View Patent ↗The present invention concerns methods for obtaining high-tenacity aramid yarn, wherein the yarn is made of a copolymer obtained from a mixture of monomers comprising 5-(6)-amino-2-(p-aminophenyl)benzimidazole, an aromatic para-diamine, and an aromatic para-diacid; the method comprising: a) spinning said copolymer from an inorganic acid solvent to produce the aramid yarn; b) washing said yarn with a basic aqueous solution for at least 5 seconds; and c) heating said yarn; wherein the yarn is heated in at least two process steps, characterized in that (i) in a first step the yarn is heated at a temperature of 200 to 360° C. at a tension of at least 0.2 cN/dtex, followed by (ii) a second step wherein the yarn is heated at a temperature of 370 to 500° C. at a tension of less than 1 cN/dtex. In some embodiments, the yarn has an effective polymer cation to sulfur content molar ratio of at least 0.3. In some embodiments, the yarn has a hydrolytic strength retention of the yarn is greater than 60%.
1. A method for obtaining high-tenacity aramid yarn, wherein the yarn is made of a copolymer obtained from a mixture of monomers comprising 5-(6)-amino-2-(p-aminophenyl)benzimidazole, an aromatic para-diamine, and an aromatic para-diacid; said method comprising:
a) spinning a dope solution comprising said copolymer and sulfuric acid to produce the aramid yarn;
b) washing said yarn with a basic solution for at least 5 a time period of greater than 20 seconds; and
c) heating said yarn; wherein the yarn is heated in at least two process steps, characterized in that
in a first step the yarn is heated at a temperature of 200 to 360° C. at a tension of at least 0.2 cN/dtex, followed by
a second step wherein the yarn is heated at a temperature of 370 to 500° C. at a tension of less than 1 cN/dtex,
wherein the hydrolytic strength retention of the yarn is greater than 60%; and
wherein the hydrolytic strength retention is computed by dividing the strength of a skein of yarn treated with saturated steam at 150° C. for 24 hours by the strength of an untreated skein of yarn and multiplying by 100.
2. The method of claim 1 further comprising washing said yarn with water before and after contacting said yarn with said basic aqueous solution.
3. The method of claim 1 , wherein the first heating step is performed at 240 to 330° C. at a tension of at least 3 cN/dtex.
4. The method of claim 1 , wherein the second heating step is performed at 400 to 470° C. at a tension less than 0.5 cN/dtex.
5. The method of claim 1 , wherein the copolymer is obtained from a mixture of monomers at least comprising a) 5-(6)-amino-2-(p-aminophenyl)-benzimidazole, b) terephthaloyl dichloride and/or 2-chloroterephthaloyl dichloride, and c) p-phenylene diamine and/or 2-chloro-p-phenylenediamine.