Method of manufacturing a timber composite, the timber composite obtained and decorative panels comprising such timber composite
A method of manufacturing a timber composite ( 7 ) is disclosed. The method comprises the steps of applying adhesive to one or more timber layers ( 23 - 226 ), applying pressure to the one or more timber layers, and heating the timber layers. The adhesive penetrates into the one or more timber layers and cures to form the timber composite ( 7 ). One or more spacers ( 332 ) may be positioned between the timber layers. The invention also related to timber composite ( 7 ) obtainable by such method and to decorative panels ( 1 ) comprising such timber composite ( 7 ) as a top layer.
1. A method of manufacturing a timber composite, the method comprising the steps of:
cutting one or more timber pieces to form a plurality of timber layers;
applying adhesive to the plurality of timber layers;
arranging the plurality of timer layers in a stack;
applying pressure to the timber layers; and
heating the timber layers,
such that the adhesive penetrates into the one or more timber layers and cures to form the timber composite, wherein the timber layers are arranged in the stack in their original order and orientation in the timber piece from which they are cut, and wherein the adhesive is a thermosetting adhesive.
2. The method of claim 1 , wherein the adhesive penetrates such that it is distributed generally evenly throughout the one or more timber layers.
3. The method of claim 1 , wherein the cutting is one of rotary peeling, slicing or saw cutting.
4. The method of claim 1 , wherein each timber layer has a thickness of 0.2 mm to 1 mm.
5. The method of claim 1 , wherein the timber has a moisture content of 8% to 12% prior to the application of pressure and heat.
6. The method of claim 1 , wherein the adhesive is based on melamineformaldehyde, ureumformaldehyde, meamine-ureumformaldehyde or phenolformaldehyde.
7. The method of claim 1 , wherein the adhesive is applied to one or both sides of or each timber layer.
8. The method of claim 1 , wherein the pressure applied to the timber is between 0.1 MPa and 30 MPa.
9. The method of claim 1 , wherein the timber is heated to a maximum temperature of between 50° C. and 250° C.
10. The method of claim 1 , wherein the timber is gradually heated to allow the adhesive to fully penetrate the one or more timber layers.
11. The method of claim 1 , wherein, when the step of heating the timber is performed, the temperature of the timber is increased from room temperature to a maximum temperature gradually over a period of 20 to 60 minutes.
12. The method of claim 1 , further comprising the steps of cooling the timber and releasing the pressure, wherein the pressure is only released once the temperature of the timber has returned to approximately room temperature.
13. The method of claim 1 , further comprising the step of positioning a spacer between two timber layers.
14. The method of claim 13 , wherein the adhesive is applied to a plurality of timber layers, the spacer positioned such that a stack of timber layers is formed on either side of the spacer.
15. The method of claim 14 , wherein each stack of layers is cut from a different timber piece.
16. The method of claim 14 wherein each stack of layers on either side of the spacer is arranged in the original order from which they are produced from the timber piece(s), such that a natural grain of each stack is maintained.
17. The method of claim 13 , wherein the spacer is a sheet of cardboard, plastic or soft metal.
18. The method of claim 1 , further comprising the step of applying a stain to the one or more timber layers prior to applying an adhesive to the one or more timber layers.
19. The method of claim 18 , wherein the stain is applied so as to penetrate into and be distributed evenly throughout the one or more timber layers.
20. A timber composite comprising timber layers and an adhesive matrix, at least one surface of the timber composite having raised portions of summer wood and depressed portions of spring wood.
21. A decorative panel comprising a substrate material and a decorative top layer, wherein the top layer is formed by a timber composite comprising a plurality of timber layers obtained from a same timber piece and penetrated with a cured thermosetting adhesive, wherein said timber layers are available in said top layer in their original order in which they were cut from said timber piece.
22. The decorative panel of claim 21 , wherein for said timber composite use is made of a timber composite in accordance with claim 20 .
23. The method of claim 1 , wherein the adhesive contains formaldehyde, sodium hydroxide, urea, melamine, polyvinyl alcohol, polyolefine, polyamide adhesive, polyurethane or asphalt.
24. The method of claim 1 , wherein a high density timber composite is obtained in that the density of the timber composite is increased compared to the timber pieces or timber layers.
25. The method of claim 8 , wherein the pressure applied to the timber is between 2 MPa and 10 MPa.
26. The method of claim 9 , wherein the timber is heated to a maximum temperature of between 100° C. and 200° C.