Positive electrode for a lithium ion capacitor and lithium ion capacitor
A positive electrode for a lithium ion capacitor includes a positive electrode layer which, after a pretreatment for measurement, has a volume of pores having pore size of not lower than 1.0 nm and lower than 1.4 nm of not lower than 0.11 cc/g, calculated by an HK method, and total pore volume calculated by a BET method of not more than 1.1 cc/g. In the pretreatment: the positive electrode is taken out of a cell of cell voltage of 3 V, cut out and immersed in 10 cc of dehydrated acetonitrile per 1 cm 3 of the positive electrode at 25° C. for 10 minutes with stirring. This immersion is repeated three times, and the positive electrode is in a pre-drying at 60° C. for 1 hour. The positive electrode layer is then scraped off from the positive electrode and dried for 2 hours at 200° C. and pressure reduced to 5.5 Pa.
1. A positive electrode for a lithium ion capacitor, the positive electrode comprising:
a positive electrode layer (A) which, after a following pretreatment for measurement, has a volume of pores having a pore size of 1.0 nm to 1.4 nm and of 0.11 cc/g or more, the pore size being calculated by a Horvath-Kawazoe (HK) method, and has a total pore volume calculated by a Brunauer-Emmett-Teller (BET) method of 1.1 cc/g or less, wherein
in the pretreatment for measurement:
the positive electrode is taken out of a cell having a cell voltage of 3 V, cut out and then immersed in 10 cc (mL) of dehydrated acetonitrile per 1 cm 3 of the positive electrode at 25° C. for 10 minutes with stirring; this immersion is repeated three times and the positive electrode is subjected to a pre-drying treatment at 60° C. for 1 hour; and the positive electrode layer (A) is scraped off from the positive electrode obtained by the pre-drying treatment and dried for 2 hours under conditions of 200° C. and a pressure reduced to 5.5 Pa.
2. The positive electrode for a lithium ion capacitor according to claim 1 , wherein the positive electrode layer (A) has a BET specific surface area calculated by the BET method of 1500 m 2 /g to 2000 m 2 /g.
3. The positive electrode for a lithium ion capacitor according to claim 1 , wherein the positive electrode layer (A) has a volume of pores, having a pore size calculated by the HK method of 0.6 nm to 1.0 nm, and of 0.23 cc/g or less.
4. A lithium ion capacitor, comprising:
the positive electrode according to claim 1 ; and
an electrolyte solution containing a cyclic carbonate and a chain carbonate.
5. The lithium ion capacitor according to claim 4 , wherein the electrolyte solution contains the cyclic carbonate of 20 to 70 vol % and the chain carbonate of 30 to 80 vol % in terms of a volume ratio as a solvent.
6. A positive electrode for a lithium ion capacitor, the positive electrode comprising:
a positive electrode layer (B), wherein, in the positive electrode before being incorporated into a cell, the positive electrode layer (B), after a following pretreatment for measurement, has a volume of pores having a pore size of 1.0 nm to 1.4 nm and of 0.13 cc/g or more, the pore size being calculated by a Horvath-Kawazoe (HK) method, and has a total pore volume calculated by a Brunauer-Emmett-Teller (BET) method of 1.2 cc/g or less, wherein
in the pretreatment for measurement:
the positive electrode layer (B) is scraped off and dried for 2 hours under conditions of 200° C. and a pressure reduced to 5.5 Pa.
7. The positive electrode for a lithium ion capacitor according to claim 6 , wherein the positive electrode layer (B) has a BET specific surface area calculated by the BET method within a range of 1900 to 2300 m 2 /g.
8. The positive electrode for a lithium ion capacitor according to claim 6 , wherein the positive electrode layer (B) has a volume of pores, having a pore size of 0.6 nm to 1.0 nm calculated by the HK method, and of 0.27 cc/g or less.
9. A lithium ion capacitor, comprising:
the positive electrode according to claim 6 ; and
an electrolyte solution containing a cyclic carbonate and a chain carbonate.
10. The lithium ion capacitor according to claim 9 , wherein the electrolyte solution contains the cyclic carbonate of 20 to 70 vol % and the chain carbonate of 30 to 80 vol % in terms of a volume ratio as a solvent.