Porous carbon material for electrode of energy storage device and method for manufacturing said material
A porous carbon material for electrodes of energy storage devices comprising: a porous carbon material; 0.5 to 5 parts by mass of an insulating material having a boiling point of 150° C. or more based on 100 parts by mass of the porous carbon material; and 0.25 to 15 parts by mass of a conductive additive based on 100 parts by mass of the insulating material, wherein the insulating material and the conductive additive are carried on the porous carbon material in combination, and the porous carbon material has a BET specific surface area of 1300 to 2050 m 2 /g.
1. A porous carbon material composition for electrodes of energy storage devices, the porous carbon material composition comprising:
a porous carbon material;
0.5 to 5 parts by mass of an insulating material having a boiling point of 150° C. or more based on 100 parts by mass of the porous carbon material; and
0.25 to 15 parts by mass of a conductive additive based on 100 parts by mass of the insulating material,
wherein:
the insulating material and the conductive additive are carried on the porous carbon material in combination; and
the porous carbon material has a BET specific surface area of 1300 to 2050 m 2 /g, and
wherein, kinetic viscosity at 25° C. of the insulating material is 1 to 1000 mm 2 /s.
2. The porous carbon material composition according claim 1 , wherein pour point of the insulating material is −30° C. or less.
3. The porous carbon material composition according to claim 1 , wherein the insulating material is a siloxane compound having siloxane units in a main chain.
4. The porous carbon material composition according to claim 1 , wherein a high-molecular compound is also carried in combination.
5. An electrode, comprising the porous carbon material composition of claim 1 .
6. An energy storage device, comprising the electrode of claim 5 .
7. A method for manufacturing a porous carbon material composition for electrodes of energy storage devices, the method comprising contacting a porous carbon material with an insulating material and a conductive additive,
wherein:
the porous carbon material has a BET specific surface area of 1300 to 2050 m 2 /g,
kinetic viscosity at 25° C. of the insulating material is 1 to 1000 mm 2 /s;
the composition comprises 0.5 to 5 parts by mass of the insulating material having a boiling point of 150° C. or more based on 100 parts by mass of the porous carbon material;
the composition comprises 0.25 to 15 parts by mass of the conductive additive based on 100 parts by mass of the insulating material; and
the insulating material and the conductive additive are carried on the porous carbon material.
8. The method according to claim 7 , wherein the insulating material and the conductive additive are added to the porous carbon material to be carried on the porous carbon material.
9. The method according to claim 7 , wherein a mixture comprising the insulating material and the conductive additive are added to the porous carbon material to be carried on the porous carbon material.
10. The method according to claim 7 , wherein the insulating material and the conductive additive are carried on the porous carbon material by dipping the porous carbon material into a mixture comprising the insulating material and the conductive additive.
11. The method according to claim 9 , wherein the mixture further comprises a high-molecular compound.