Polyamide resin and molded article containing same
The present invention relates to a polyamide resin comprising a unit derived from ε-caprolactam and/or ε-aminocaproic acid (to also be referred to as “Unit 1”), a unit derived from adipic acid (to also be referred to as “Unit 2”) and a unit derived from hexamethylenediamine (to also be referred to as “Unit 3”), wherein the concentration of terminal amino groups in the polyamide resin is greater than the concentration of terminal carboxyl groups in the polyamide resin, and the amount of Unit 1 is greater than 60% by weight to less than 80% by weight of the total amount of Unit 1, Unit 2 and Unit 3.
1. A polyamide resin consisting of a unit derived from ε-caprolactam and/or ε-aminocaproic acid (to also be referred to as “Unit 1”), a unit derived from adipic acid (to also be referred to as “Unit 2”) and a unit derived from hexamethylenediamine (to also be referred to as “Unit 3”), wherein the concentration of terminal amino groups in the polyamide resin is greater than the concentration of terminal carboxyl groups in the polyamide resin, and the amount of Unit 1 is greater than 60% by weight to less than 80% by weight of the total amount of Unit 1, Unit 2 and Unit 3, and wherein the polyamide resin has the following features (1) and (2):
(1) relative viscosity (ηr) of the polyamide resin measured in 96% by weight of sulfuric acid under conditions of a polyamide concentration of 1% by weight and temperatures of 25° C. is 3.4 or more; and
(2) the concentration of terminal carboxyl groups in the polyamide resin is 2.00×10 −5 eq/g to 3.00×10 −5 eq/g, provided that the concentration of terminal amino groups in the polyamide resin is greater than the concentration of terminal carboxyl groups in the polyamide resin.
2. The polyamide resin according to claim 1 , wherein the concentration of terminal amino groups is 2.30×10 −5 eq/g to 3.30×10 −5 eq/g, provided that the concentration of terminal amino groups in the polyamide resin is greater than the concentration of terminal carboxyl groups in the polyamide resin.
3. The polyamide resin according to claim 1 , wherein the difference between the concentration of terminal amino groups and the concentration of terminal carboxyl groups is 0.05×10 −5 eq/g to 1.0×10 −5 eq/g.
4. A molded article comprising:
a) the polyamide resin according to claim 1 , or
b) a polyamide resin composition comprising the polyamide resin according to claim 1 .
5. A non-stretched polyamide film comprising:
a) the polyamide resin according to claim 1 , or
b) a polyamide resin composition comprising the polyamide resin according to claim 1 .
6. A stretched polyamide film obtained by stretching the non-stretched film according to claim 5 .
7. The non-stretched polyamide film according to claim 5 , which is a food packaging film.
8. The stretched polyamide film according to claim 6 , which is a food packaging film.
9. A multi-layered film comprising the non-stretched polyamide film according to claim 5 .
10. A multi-layered film comprising the stretched polyamide film according to claim 6 .
11. A polyamide monofilament comprising:
a) the polyamide resin according to claim 1 , or
b) a polyamide resin composition comprising the polyamide resin according to claim 1 .
12. A polyamide resin composition comprising the polyamide resin according to claim 1 .