MOLTEN AL PLATED STEEL WIRE AND STRAND WIRE, AND METHOD FOR PRODUCING SAME
A molten Al plated steel wire excellent in torsional resistance that does not cause breakage due to torsion in application to an ordinary production equipment for a strand wire, in which element wires are applied with torsion is provided. A molten Al plated steel wire containing a steel core wire having a diameter of from 0.05 to 0.50 mm as a core material, having thereon molten Al plating with a depositing amount thereof that is uniformized to satisfy the following expression (1) for an average diameter D A (mm) and a minimum diameter D MIN (mm) in the longitudinal direction of the wire: (D A −D MIN )/D A 0.10.
1 . A molten Al plated steel wire comprising a steel core wire having a diameter of from 0.05 to 0.50 mm as a core material, wherein an average diameter D A (mm) and a minimum diameter D MIN (mm) in the longitudinal direction of the wire satisfy the following expression (1):
( D A −D MIN )/ D A ≦0.10 (1)
2 . The molten Al plated steel wire according to claim 1 , wherein the molten Al plated steel wire is not subjected to a wire drawing process after applying to the molten Al plating.
3 . A strand wire comprising the molten Al plated steel wire according to claim 1 as an element wire that is stranded with other element wires in a state where the molten Al plated steel wire is applied with torsion.
4 . A method for producing a strand wire, comprising twisting the molten Al plated steel wire according to claim 1 as an element wire with other element wires in a state where the molten Al plated steel wire is applied with torsion.