Thermoplastic resin composition for matting, fluorine-based matte film, and fluorine-based matte layered film
Provided are a thermoplastic resin composition whereby gum formation is suppressed during manufacturing of a matte fluororesin molded article such as a film, and a fluorine-based matte film having excellent matte properties and chemical resistance, and a layered film. A thermoplastic resin composition (α) for a chemical-resistant matte film, comprising a fluorine-based resin (A), a matting agent (B) which is a thermoplastic resin insoluble in the fluorine-based resin (A), and a thermoplastic resin (C) soluble in the fluorine-based resin (A). A thermoplastic resin composition (β) containing the fluorine-based resin (A) and an acrylic matting agent (D) which is a thermoplastic resin, the content ratio of alkyl acrylate units with respect to 100% by mass of monofunctional monomer units in the monomer units constituting the matting agent (D) being 50-100% by mass, and the content ratio of other monofunctional monomer units being 0-50% by mass. A matte film molded from the abovementioned thermoplastic resin compositions. A layered film in which an acrylic resin is layered on the matte film.
1. A thermoplastic resin composition (α), comprising:
a fluorine-based resin (A);
a matting agent (B) which is a thermoplastic resin insoluble in the fluorine-based resin (A); and
a thermoplastic resin (C-1) soluble in the fluorine-based resin (A),
wherein the thermoplastic resin (C-1) comprises monomer units derived from:
50 to 100% by mass of alkyl methacrylate;
optionally, 0 to 50% by mass of alkyl acrylate; and
optionally, 0 to 49% by mass of at least one monomer selected from the group consisting of a (meth)acrylic monomer, an aromatic vinyl monomer and a vinyl cyanide monomer,
wherein the matting agent (B) is contained in the thermoplastic resin composition (α) at 1 to 50 parts by mass and the thermoplastic resin (C-1) is contained in the thermoplastic resin composition (α) at 30 to 70 parts by mass, relative to 100 parts by mass of the fluorine-based resin (A).
2. The thermoplastic resin composition (α) according to claim 1 , wherein the matting agent (B) is a non-crosslinked acrylic resin comprising a hydroxy group.
3. The thermoplastic resin composition (α) according to claim 1 , wherein the thermoplastic resin (C-1) does not contain a hydroxy group.
4. The thermoplastic resin composition (α) according to claim 1 , wherein the composition satisfies the following relationship:
5.2< SP ( B )− SP ( AC )<6.6
wherein SP (AC) is an SP value of the fluorine-based resin (A) and the thermoplastic resin (C-1) and SP (B) is an SP value of the matting agent (B).
5. The thermoplastic resin composition (α) according to claim 2 , wherein a hydroxy number of the non-crosslinked acrylic resin comprising a hydroxy group is 50 to 200 mgKOH/g.
6. The thermoplastic resin composition (α) according to claim 1 , wherein the composition satisfies the following relationship:
MFR ( A )> MFR ( C )> MFR ( B )
wherein MFR (A), MFR (B), and MFR (C) are an MFR of the fluorine-based resin (A), an MFR of the matting agent (B), and an MFR of the thermoplastic resin (C-1), at 250° C. and a load of 49 N, respectively.
7. A thermoplastic resin composition (β), comprising:
a fluorine-based resin (A); and
a acrylic matting agent (D) as a thermoplastic resin,
wherein a content ratio of acrylic acid alkyl ester is 50 to 100% by mass and a content ratio of other monofunctional monomer unit is 0 to 50% by mass, when monofunctional monomer units in the monomer unit constituting the acrylic matting agent (D) is 100% by mass.
8. The thermoplastic resin composition (α) according to claim 1 , wherein the fluorine-based resin (A) is a vinylidene fluoride polymer.
9. A fluorine-based matte film obtained by molding the thermoplastic resin composition (α) according to claim 1 .
10. A fluorine-based matte layered film obtained by layering the fluorine-based matte film according to claim 9 and the acrylic resin (H).
11. The fluorine-based matte film according to claim 9 , wherein 60 degree surface gloss is 5 to 80 on a matte surface.
12. The fluorine-based matte film according to claim 9 , wherein 60 degree surface gloss standard deviation is 6 or less.
13. The thermoplastic resin composition (α) according to claim 1 , wherein thermoplastic resin (C-1) consists of monomer units derived from:
50 to 100% by mass of alkyl methacrylate;
optionally, 0 to 50% by mass of alkyl acrylate; and
optionally, 0 to 49% by mass of at least one monomer selected from the group consisting of a (meth)acrylic monomer, an aromatic vinyl monomer and a vinyl cyanide monomer.