Composite body and method for producing same
A composite production method includes impregnating a plate-shaped porous inorganic structure and a fibrous inorganic material with a metal while the fibrous inorganic material is arranged to be adjacent to the porous inorganic structure. In the composite structure, first and second phases are adjacent to each other by using a porous inorganic structure having a porous silicon carbide ceramic sintered body and the fibrous inorganic material, the first phase being a phase in which the porous silicon carbide ceramic sintered body is impregnated with the metal, the second phase being a phase in which the fibrous inorganic material is impregnated with the metal, a percentage of the porous silicon carbide ceramic sintered body in the first phase is 50 to 80 volume percent, and a percentage of the fibrous inorganic material in the second phase is 3 to 20 volume percent. A composite is produced by the method.
1. A production method for a composite comprising impregnating a plate-shaped porous inorganic structure and a fibrous inorganic material with a metal while the fibrous inorganic material is arranged so as to be adjacent to the porous inorganic structure, wherein
the composite has a structure in which a first phase and a second phase are adjacent to each other by using the porous inorganic structure comprising a porous silicon carbide ceramic sintered body and the fibrous inorganic material having a porosity of 80 to 97volume percent, the first phase being a phase in which the porous silicon carbide ceramic sintered body is impregnated with the metal, the second phase being a phase in which the fibrous inorganic material is impregnated with the metal,
a percentage of the porous silicon carbide ceramic sintered body in the first phase is 50 to 80 volume percent, and
a percentage of the fibrous inorganic material in the second phase is 3 to 20 volume percent.
2. The production method for the composite according to claim 1 , wherein the method for the impregnation with the metal is a die casting method or a squeeze casting method.
3. The production method for the composite according to claim 1 , wherein the metal is aluminum or an aluminum alloy.
4. The production method for the composite according to claim 1 , wherein a thickness of a layer comprising the second phase is 1 mm or more.
5. The production method for the composite according to claim 1 , wherein all surfaces of a circumference of the porous silicon carbide ceramic sintered body are covered with the fibrous inorganic material, or the porous silicon carbide ceramic sintered body is sandwiched between two sheets of the fibrous inorganic material.
6. The production method for the composite according to claim 1 , wherein the porosity of the fibrous inorganic material is 82 to 94 volume percent.
7. The production method for the composite according to claim 1 , wherein a porosity of the porous silicon carbide ceramic sintered body is set to 20 to 50 volume percent.
8. A composite having a structure in which a first phase and a second phase are adjacent to each other, the first phase being a phase in which a plate-shaped porous inorganic structure comprising a porous silicon carbide ceramic sintered body is impregnated with a metal, the second phase being a phase in which a fibrous inorganic material having a porosity of 80 to 97 volume percent is impregnated with the metal,
a percentage of the porous silicon carbide ceramic sintered body in the first phase being 50 to 80 volume percent,
a percentage of the fibrous inorganic material in the second phase being 3 to 20 volume percent.
9. The composite according to claim 8 , wherein the metal is aluminum or an aluminum alloy.
10. The composite according to claim 8 , wherein a thickness of a layer comprising the second phase is 1 mm or more.
11. The composite according to claim 8 , wherein all surfaces of a circumference of the first phase are covered with the second phase, or the first phase is formed on only front and back plate surfaces of the second phase.
12. The composite according to claim 8 , wherein the porosity of the fibrous inorganic material is 82 to 94 volume percent.
13. The composite according to claim 8 , wherein a porosity of the porous silicon carbide ceramic sintered body is set to 20 to 50 volume percent.