Multi-layered aluminium brazing sheet material
View Patent ↗Multilayered brazing sheet material including an aluminum core alloy layer having a first brazing clad layer material on one face of the core layer and a second brazing clad layer material on the other face of the core material, and an inter-layer between the core layer and the first brazing clad layer material, wherein the core layer is 3xxx-series aluminum alloy having, in wt. %, up to 0.4% Si, up to 0.5% Fe, 0.4% to 0.75% Cu, 0.6% to 1.1% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.2% Ti, up to 0.15% Zn, balance aluminum and impurities, wherein the first brazing layer and the second brazing layer are 4xxx-series aluminum alloy having 7% to 14% Si and up to 2% Mg, balance aluminum and impurities, and wherein the inter-layer is aluminum alloy of the 1xxx-series alloys.
1. A multi-layered brazing sheet material consisting of an aluminium core alloy layer provided with a first brazing clad layer material on one face of said aluminium core alloy layer and a second brazing clad layer material on another face of said aluminium core alloy layer, and an inter-layer positioned between the aluminium core alloy layer and the first brazing clad layer material,
wherein the aluminium core alloy layer is made from a 3xxx-series aluminium alloy having, in wt. %, up to 0.4% Si, up to 0.5% Fe, 0.4% to 0.75% Cu, 0.6% to 1.0% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.2% Ti, and up to 0.15% Zn, balance aluminium and impurities,
wherein the first brazing clad layer material and the second brazing clad layer material are made from a 4xxx-series aluminium alloy having 6% to 14% Si, up to 2% Mg, and up to 0.20% Zn, balance aluminium and impurities, and
wherein the inter-layer is made from an aluminium alloy of the 1xxx-series alloys having a Zn content of less than 0.1%.
2. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer is made from an aluminium alloy consisting of, in wt. %, up to 0.2% Si, 0.15% to 0.45% Fe, 0.50 to 0.7% Cu, 0.7% to 1.0% Mn, up to 0.02% Mg, up to 0.09% Cr, up to 0.09% Zr, 0.05% to 0.2% Ti, and up to 0.15% Zn, balance aluminium and impurities.
3. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer is made from an aluminium alloy consisting of, in wt. %, up to 0.2% Si, 0.25% to 0.45% Fe, 0.50% to 0.68% Cu, 0.7% to 0.95% Mn, up to 0.02% Mg, up to 0.04% Cr, up to 0.04% Zr, 0.06% to 0.12% Ti, and up to 0.15% Zn, balance aluminium and impurities.
4. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material is made from a 4xxx-series aluminium alloy having 6% to 11% Si and up to 0.35% Mg.
5. The brazing sheet material according to claim 1 , wherein the inter-layer has a thickness of 60 μm or less.
6. The brazing sheet material according to claim 1 , wherein the inter-layer is made from an aluminium alloy of the 1xxx-series alloys having a Zn-content of less than 0.05%.
7. The brazing sheet material according to claim 1 , wherein the brazing sheet material has a total thickness of 0.1 to 1.2 mm.
8. The brazing sheet material according to claim 7 , wherein each of the first and second brazing clad layer materials has a thickness of 5% to 15% of the total thickness.
9. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer has been homogenised.
10. The brazing sheet material according to claim 1 , wherein the brazing sheet material is provided in an O-temper.
11. A brazing tube made from the multi-layered brazing sheet material according to claim 1 .
12. A heat exchanger comprising a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
13. A charge-air-cooler incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
14. A water charge-air-cooler incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
15. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material and the second brazing clad layer material are each made from a 4xxx-series aluminium alloy having 6% to 11% Si and up to 0.35% Mg, balance impurities and aluminium.
16. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material and the second brazing clad layer material are each made from a 4xxx-series aluminium alloy having 6% to 11% Si and up to 0.10% Mg, balance impurities and aluminium.
17. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material is made from a 4xxx-series aluminium alloy having 6% to 11% Si and up to 0.10% Mg, balance impurities and aluminium.
18. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer has a Fe content of 0.25-0.45% Fe.
19. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer has a Mn content of 0.6% to 0.95%.
20. The brazing sheet material according to claim 1 , wherein the Zn of the first brazing clad layer material and the second brazing clad layer material if present is not a purposefully added impurity.