Composite nanoparticles for roofing granules, roofing shingles containing such granules, and process for producing same
Processes for making algaecidal roofing granules are disclosed. In one aspect, the disclosure provides a method includes providing composite nanoparticles comprising algaecidal nanoparticles and a carrier material; coating granule cores with the coating material to form a coating layer having an exterior surface; and applying the composite nanoparticles to the exterior surface of the coating layer to provide the algaecidal nanoparticles at exterior surfaces of the algaecidal roofing granules. In another aspect of the disclosure, a method includes dispersing composite nanoparticles in a coating material, the composite nanoparticles including a carrier material and algaecidal nanoparticles, then coating the granule cores with the coating material to form a coating layer; and curing the coating layer, the cured coating layer providing algaecidal nanoparticles at exterior surfaces of the algaecidal roofing granules.
1. A process for preparing algaecidal roofing granules, the process comprising
providing:
granule cores;
a coating material comprising an alkali metal silicate and a curing agent for the alkali metal silicate; and
composite nanoparticles comprising algaecidal nanoparticles and an alkali metal silicate dispersible in the coating material, the algaecidal nanoparticles being nanoparticles of silver, silver oxide, copper, copper oxide, zinc, or zinc oxide; and
for each of a plurality of the granule cores,
coating the granule core with the coating material to form on the granule core a layer of the coating material having an exterior surface;
applying the composite nanoparticles to the exterior surface of the layer of coating material; and
curing the layer of coating material to provide a coating,
thereby providing a plurality of algaecidal roofing granules, each comprising at an exterior surface a coating comprising algaecidal nanoparticles.
2. A process for preparing algaecidal roofing granules according to claim 1 , the process further comprising forming the composite nanoparticles by a process comprising:
(a) providing the algaecidal nanoparticles;
(b) providing the alkali metal silicate;
(c) forming a mixture by dispersing the algaecidal nanoparticles in the alkali metal silicate; and
(d) forming the composite nanoparticles from the mixture of step (c).
3. A process for preparing algaecidal roofing granules according to claim 1 , the process further comprising forming the composite nanoparticles by a process comprising:
(a) providing the algaecidal nanoparticles;
(b) providing carrier particles having exterior surfaces, the carrier particles including the alkali metal silicate; and
(c) adhering the algaecidal nanoparticles to the exterior surfaces of the carrier particles.
4. A process for preparing algaecidal roofing granules according to claim 1 , the process further comprising forming the composite nanoparticles by a process comprising:
(a) providing the algaecidal nanoparticles;
(b) providing carrier particles, the carrier particles comprising the alkali metal silicate;
(c) mixing the algaecidal nanoparticles and the carrier particles; and
(d) aggregating the carrier particles so as to trap the nanoparticles among the aggregated carrier particles.
5. A process for preparing algaecidal roofing granules according to claim 1 , the process further comprising forming the composite nanoparticles by a process comprising:
(a) providing the algaecidal nanoparticles;
(b) providing porous carrier particles, the carrier particles including the alkali metal silicate; and
(c) entrapping the algaecidal nanoparticles in the pores of the carrier particles.
6. A process for preparing algaecidal roofing granules according to claim 1 , wherein the process further comprising forming the composite nanoparticles by a process comprising:
(a) providing the algaecidal nanoparticles;
(b) providing the alkali metal silicate;
(c) coating the algaecidal nanoparticles with the alkali metal silicate; and
(d) aggregating the coated algaecidal nanoparticles to form green composite nanoparticles.
7. A process for preparing algaecidal roofing granules according to claim 1 , wherein the algaecidal nanoparticles are nanoparticles of silver, silver oxide, copper, or copper oxide.
8. A process for preparing algaecidal roofing granules according to claim 1 , wherein the composite nanoparticles include sodium silicate as the alkali metal silicate.
9. A process for preparing algaecidal roofing granules according to claim 1 , wherein the composite nanoparticles include at least one curing agent selected from the group consisting of kaolin clays, metal phosphates, aluminum fluoride, and sodium fluorosilicates, and combinations thereof.
10. A process for preparing algaecidal roofing granules according to claim 1 , wherein the composite nanoparticles have an average size of from about 0.1 micrometers to about 100 micrometers.
11. A process for preparing algaecidal roofing granules according to claim 1 , wherein the composite nanoparticles have an average weight density of nanoparticles of from about 0.05 grams of algaecidal nanoparticles per gram of carrier material to about 0.7 grams of algaecidal nanoparticles per gram of carrier material.
12. The process of claim 1 , wherein the curing agent is a heat-reactive aluminosilicate.
13. The process of claim 1 , wherein the composite nanoparticles further include a heat-reactive aluminosilicate.
14. A process for preparing algaecidal roofing granules, the process comprising
providing:
granule cores;
a coating material comprising an alkali metal silicate and a curing agent for the alkali metal silicate;
composite nanoparticles comprising algaecidal nanoparticles and an alkali metal silicate dispersible in the coating material, the algaecidal nanoparticles being nanoparticles of silver, silver oxide, copper, copper oxide, zinc, or zinc oxide; and
for each of a plurality of the granule cores,
coating the granule core with the coating material to form on the granule core a layer of the coating material having an exterior surface;
applying the composite nanoparticles to the exterior surface of the layer of coating material; and
curing the layer of coating material,
thereby providing a plurality of algaecidal roofing granules, each comprising a coating comprising algaecidal nanoparticles at an exterior surface of the algaecidal roofing granule;
and then
embedding the plurality of algaecidal roofing granules having the coating having the coating at the exterior surfaces thereof comprising the algaecidal nanoparticles in the surface of a bituminous roofing product.
15. A process for preparing algaecidal roofing granules according to claim 14 , wherein the algaecidal nanoparticles are nanoparticles of silver, silver oxide, copper, or copper oxide.
16. A process for preparing algaecidal roofing granules according to claim 14 , wherein the composite nanoparticles include sodium silicate as the alkali metal silicate.
17. A process for preparing algaecidal roofing granules according to claim 14 , wherein the composite nanoparticles include at least one curing agent selected from the group consisting of kaolin clays, metal phosphates, aluminum fluoride, and sodium fluorosilicates, and combinations thereof.
18. A process for preparing algaecidal roofing granules according to claim 14 , wherein the composite nanoparticles have an average size of from about 0.1 micrometers to about 100 micrometers.
19. A process for preparing algaecidal roofing granules according to claim 14 , wherein the composite nanoparticles have an average weight density of nanoparticles of from about 0.05 grams of algaecidal nanoparticles per gram of carrier material to about 0.7 grams of algaecidal nanoparticles per gram of carrier material.
20. The process of claim 14 , wherein the curing agent is a heat-reactive aluminosilicate.
21. The process of claim 14 , wherein the composite nanoparticles further include a heat-reactive aluminosilicate.