Aqueous primer composition for enhanced film formation and method of using the same

View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 9,803,089
App. No.
15/340,475
Granted
Oct 31, 2017
Kind
B2
Abstract

A water-based bonding primer composition and a method of applying the same onto a metallic surface prior to adhesive bonding. The bonding primer composition is a water-based dispersion containing water, one or more epoxy resins, one or more curing agents, a silane compound, a low amount of propylene carbonate (PC), and optional additives. The bonding primer composition can form substantially smooth films by spraying, and at the same time, meet environmental regulations and provide high bonding performance.

Claims (14)

1. A water-based primer composition that has a pH within the range of 6-8 and can be sprayed, the primer composition comprising:

(i) 20-60 wt. % one or more epoxy resins;

(ii) 2-30 parts curing agent, solely or in combination with one or more catalysts, per 100 parts of epoxy resin(s) in total;

(iii) organosilane in an amount of 0.1 to 10 parts per 100 parts of water;

(iv) 1-10 wt. % propylene carbonate;

(v) 1-7 wt. % at least one chromate or non-chromate corrosion inhibitor; and

(vi) water to provide 10%-25% solids.

2. The water-based primer composition of claim 1 further comprising 0.1-2 wt. % of an additive selected from: inorganic fillers in particulate form, pigments, dyes, and combinations thereof.

3. The water-based primer composition of claim 1 , wherein the organosilane has following general formula:

wherein n is greater than or equal to 0; wherein X is selected from OH, OCH 3 , and OCH 2 H 5 ; wherein R 1 is CH═CH 2 , or

or CH 2 —CH 2 —CH 2 —Y, wherein Y is selected from NH 2 , SH, OH, NCO, NH—CO—NH 2 , NH—(CH 2 ) 3 NH 2 , NH-Aryl,

and wherein each R 2 is selected from alkyl, alkoxy, aryl, substituted aryl, and R 1 .

4. The water-based primer composition of claim 1 , wherein the curing agent is water-soluble, and without propylene carbonate, the pH of the primer composition would be higher.

5. The water-based primer composition of claim 1 , wherein the curing agent is selected from: amino triazine; polyamine; and dicyandiamide (DICY).