Epoxy core with expandable microspheres
View Patent ↗A method of fabricating a formed structure with expandable polymeric shell microspheres. A first plurality of polymeric shell microspheres are heated from an unexpanded state to an expanded state to form a plurality of expanded microspheres. The plurality of expanded microspheres are mixed with an epoxy resin and a second plurality of unexpanded polymeric shell microspheres. The mixture is formed in a shape to create a preform. The preform is wrapped with fiber tape to create a wrapped preform. The wrapped preform is placed in a mold. The mold is heated and the second plurality of unexpanded microspheres expand from an unexpanded state to an expanded state. The mold is cooled and the formed structure is removed from the mold.
1. A method of fabricating a hockey blade, comprising:
forming a mixture of a plurality of expanded microspheres, a second plurality of unexpanded polymeric shell microspheres and forming the mixture in a shape to create a preform for an internal core;
wrapping the preform with fiber tape to create a wrapped preform smaller than the hockey blade and approximating a final geometry of the hockey blade;
placing the wrapped preform in a mold;
heating the mold and expanding the second plurality of unexpanded microspheres from an unexpanded state to an expanded state such that the mixture compresses and consolidates the fiber tape and the mixture bonds to the fiber tape;
cooling the mold; and
removing a formed structure from the mold.
2. The method according to claim 1 wherein the formed structure is a hockey blade.
3. The method according to claim 2 wherein said fiber tape is preimpregnated with resin.
4. The method according to claim 3 wherein the preform comprises a first face surface, a second face surface, a first edge surface and a second edge surface, and the fiber tape extends continuously around the first face surface, the first edge surface, the second face surface and the second edge surface.
5. The method according to claim 1 wherein the unexpanded polymeric shell microspheres are about 10-12 microns in diameter prior to heating, and are expanded to a diameter of about 40-50 microns during heating.
6. The method of claim 1 wherein the mixture has the consistency of modeling clay.
7. A method of fabricating a hockey blade with expandable thermoplastic microspheres, comprising:
forming a mixture of partially expanded microspheres with a resin, and a second plurality of unexpanded thermoplastic microspheres to form a viscous fluid material and forming the mixture in a shape to create a preform for an internal core;
wrapping the preform with fiber tape to create a wrapped preform smaller than the hockey blade and approximating a final geometry of the hockey blade;
placing the wrapped preform in a mold;
heating the mold and further expanding the plurality of partially expanded microspheres and expanding the second plurality of unexpanded microspheres such that the mixture compresses and consolidates the fiber tape and the mixture bonds to the fiber tape;
cooling the mold;
removing a formed structure from the mold.
8. The method according to claim 7 wherein said fiber tape is preimpregnated with resin.
9. The method according to claim 8 wherein the preform comprises a first face surface, a second face surface, a first edge surface and a second edge surface, the tape extending continuously around the first face surface, the first edge surface, the second face surface and the second edge surface.
10. The method according to claim 7 wherein the mixture further comprises an aramid pulp and the aramid pulp is a chopped fiber and wherein the mixture further comprises a curing agent.
11. The method according to claim 7 wherein the formed structure includes a foam insert.
12. The method according to claim 11 wherein the foam insert is placed on the preform prior to wrapping the preform with the fiber tape.
13. The method according to claim 11 wherein the foam insert is placed on a toe or a top portion of the preform.
14. The method according to claim 11 wherein the foam insert is formed of a polymethacrylimide foam.
15. The method according to claim 7 wherein the unexpanded polymeric shell microspheres are about 10-12 microns in diameter prior to heating, and are expanded to a diameter of about 40-50 microns during heating.
16. The method of claim 7 wherein the mixture has the consistency of modeling clay.