INTERLAYER FOR LAMINATED GLASS AND LAMINATED GLASS
An interlayer for a laminated glass includes a thermoplastic resin, ITO particles, and a phthalocyanine-based compound including at least one of a phthalocyanine compound and a naphthalocyanine compound. When A indicates an amount (parts by mass) of the ITO particles in 100 parts by mass of the thermoplastic resin, and B indicates an amount (parts by mass) of the phthalocyanine-based compound in 100 parts by mass of the thermoplastic resin, the amount A satisfies 0.15 (parts by mass)≦ A ≦0.3 (parts by mass) formula (1), and the amount B satisfies −0.025 A +0.012 (parts by mass)≦ B ≦−0.027 A +0.032 (parts by mass) formula (2).
1 . An interlayer for a laminated glass, the interlayer comprising:
a thermoplastic resin;
ITO particles; and
a phthalocyanine-based compound including at least one of a phthalocyanine compound and a naphthalocyanine compound, wherein
when A indicates an amount (parts by mass) of the ITO particles in 100 parts by mass of the thermoplastic resin, and B indicates an amount (parts by mass) of the phthalocyanine-based compound in 100 parts by mass of the thermoplastic resin,
the amount A satisfies
0.15 (parts by mass)≦ A≦ 0.3 (parts by mass) formula (1),
and
the amount B satisfies
−0.025 A+ 0.012 (parts by mass)≦ B≦ 0.027 A+ 0.032 (parts by mass) formula (2).
2 . A laminated glass, comprising:
a first glass substrate;
a second glass substrate; and
an interlayer that is disposed between the first glass substrate and the second glass substrate and includes
a thermoplastic resin,
ITO particles, and
a phthalocyanine-based compound including at least one of a phthalocyanine compound and a naphthalocyanine compound, wherein
when A indicates an amount (parts by mass) of the ITO particles in 100 parts by mass of the thermoplastic resin, and B indicates an amount (parts by mass) of the phthalocyanine-based compound in 100 parts by mass of the thermoplastic resin,
the amount A satisfies
0.15 (parts by mass)≦ A≦ 0.3 (parts by mass) formula (1),
and
the amount B satisfies
−0.025 A+ 0.012 (parts by mass)≦ B≦− 0.027 A+ 0.032 (parts by mass) formula (2).
3 . The laminated glass as claimed in claim 2 , wherein the laminated glass is for an automobile.