Two-layered injection molded field joint for pipeline applications
A method of coating a field joint and a coated field joint formed thereby. The field joint coating includes a first thermal insulation material injection molded over the uncoated field joint to form a first layer, and a second thermal insulation material injection molded over the first layer to form a second layer. The second material has a greater flexibility than the first material and a lower maximum operating temperature than the first material. In certain embodiments, the second material forms a significant part of the volume of the field joint coating.
1. A method of coating a field joint joining uncoated ends of two pipe sections, each pipe section being coating with a parent coating and having at least one uncoated end, the method comprising:
injection molding a first thermal insulation layer of a field joint coating over at least the uncoated ends and a portion of the parent coating of each pipe section, the first layer comprising a first material; and
injection molding a second thermal insulation layer of the field joint coating over the first layer, the second layer comprising a second material having a greater flexibility than the first material and having a lower maximum operating temperature than the first material.
2. The method of claim 1 wherein the second layer forms a majority of the field joint coating, in volume.
3. The method of claim 1 wherein the first material is an injection molded polypropylene material.
4. The method of claim 1 wherein the second material is an epoxy-urethane hybrid material.
5. The method of claim 1 wherein the first layer has a profile substantially matching an outer profile of exposed surfaces of the uncoated field joint.
6. The method of claim 4 wherein the first layer has an increased thickness in a region where the first layer overlays an angle in the exposed surfaces of the uncoated field joint.
7. The method of claim 6 wherein the increased thickness is an increase in radius in the range of about 30-50 mm.
8. The method of claim 1 wherein the first and second layers of the field joint coating are formed to create an upstand that is less than or equal to about 5 mm.
9. The method of claim 8 wherein the upstand is about 0 mm.
10. The method of claim 1 wherein:
injection molding the first layer comprises positioning a first mold about the uncoated ends and a portion of the parent coating at the field joint, the first mold corresponding to an outer profile of exposed surfaces of the uncoated field joint, and injection molding the first material into the first mold; and
injection molding the second layer comprises positioning a second mold about the first layer, and injection molding the second material into the second mold.
11. The method of claim 1 wherein the second layer is free floating over the first layer.
12. The method of claim 1 further comprising pre-treating outer surfaces of the first layer prior to injection molding the second layer, to promote bonding between the first and second layers.
13. The method of claim 1 wherein the uncoated ends are coated with a corrosion resistant coating before injection molding the first thermal insulation layer.
14. The method of claim 13 wherein the corrosion resistant coating is a fusion bonded epoxy (FBE) coating.