Grafted crosslinked cellulose
View Patent ↗Grafted, crosslinked cellulosic materials include cellulose fibers and polymer chains composed of at least one monoethylenically unsaturated acid group-containing monomer (such as acrylic acid) grafted thereto, in which one or more of said cellulose fibers and said polymer chains are crosslinked (such as by intra-fiber chain-to-chain crosslinks). Some of such materials are characterized by a wet bulk of about 10.0-17.0 cm 3 /g, an IPRP value of about 1000 to 7700 cm 2 /MPa·sec, and/or a MAP value of about 7.0 to 38 cm H 2 O. Methods for producing such materials may include grafting polymer chains from a cellulosic substrate, followed by treating the grafted material with a crosslinking agent adapted to effect crosslinking of one or more of the cellulosic substrate or the polymer chains. Example crosslinking mechanisms include esterfication reactions, ionic reactions, and radical reactions, and example crosslinking agents include pentaerythritol, homopolymers of the graft species monomer, and hyperbranched polymers.
1. A method of producing a grafted, crosslinked cellulosic material, the method comprising:
grafting polymer chains of at least one monoethylenically unsaturated acid group-containing monomer from a cellulosic substrate to produce a grafted cellulosic material; and
subsequently crosslinking the grafted cellulosic material by treating the material with a crosslinking agent adapted to effect crosslinking of one or more of the cellulosic substrate or the polymer chains;
wherein the grafting is performed in situ;
wherein the grafting includes reacting the at least one monomer with the cellulosic substrate in the presence of a grafting initiator; and
wherein the grafting initiator includes ammonium cerium(IV) sulfate.
2. The method of claim 1 , wherein the cellulosic material is cellulose fiber.
3. The method of claim 1 , wherein the grafting includes varying one or more of the weight percent of the initiator and the ratio of the cellulosic substrate to the monomer, to achieve a desired graft yield level.
4. The method of claim 1 , wherein the grafting includes using acrylic acid as the at least one monomer.
5. The method of claim 1 ,
wherein the intra-fiber crosslinking includes establishing intra-fiber crosslinks via an esterification reaction, and
wherein the crosslinking agent is selected from the group consisting of pentaerythritol, a homopolymer formed of the at least one monoethylenically unsaturated acid group-containing monomer, a hyperbranched polymer, and combinations thereof.
6. The method of claim 5 , wherein the intra-fiber crosslinking also includes establishing intra-fiber chain-to-cellulose crosslinks.
7. The method of claim 1 , wherein the intra-fiber crosslinking includes establishing intra-fiber chain-to-chain crosslinks via an ionic reaction, and wherein the crosslinking agent includes a multivalent inorganic compound.
8. The method of claim 7 , wherein the crosslinking agent includes aluminum sulfate.
9. The method of claim 1 , wherein the intra-fiber crosslinking includes establishing intra-fiber chain-to-chain crosslinks via a radical reaction, and wherein the crosslinking agent includes an inorganic salt of a strong acid and a weak base.
10. The method of claim 9 , wherein the crosslinking agent includes ammonium persulfate.
11. The method of claim 1 , further including, prior to the intra-fiber crosslinking, at least partially neutralizing the grafted polymer side chains by treating the grafted cellulosic material with an alkaline solution.
12. A method of producing a grafted, crosslinked cellulosic material, the method comprising:
grafting polymer chains of at least one monoethylenically unsaturated acid group-containing monomer from a cellulosic substrate to produce a grafted cellulosic material, wherein the polymer chains each include at least two units of the same monoethylenically unsaturated acid group-containing monomer; and
subsequently intra-fiber crosslinking the grafted cellulosic material by treating the material with a crosslinking agent adapted to effect intra-fiber crosslinking of one or more of the cellulosic substrate or the polymer chains;
wherein the intra-fiber crosslinking includes establishing intra-fiber chain-to-chain crosslinks via an ionic reaction, and wherein the crosslinking agent includes aluminum sulfate.
13. The method of claim 12 , wherein the cellulosic material is cellulose fiber.
14. The method of claim 12 , wherein the grafting is performed in situ.
15. The method of claim 14 , wherein the grafting includes reacting the at least one monomer with the cellulosic substrate in the presence of a grafting initiator.
16. The method of claim 15 , wherein the grafting initiator includes ammonium cerium(IV) sulfate.
17. The method of claim 15 , wherein the grafting includes varying one or more of the weight percent of the initiator and the ratio of the cellulosic substrate to the monomer, to achieve a desired graft yield level.
18. The method of claim 12 , wherein the grafting includes using acrylic acid as the at least one monomer.
19. The method of claim 12 , wherein the intra-fiber crosslinking also includes establishing intra-fiber crosslinks via an esterification reaction, and
wherein the crosslinking agent is selected from the group consisting of pentaerythritol, a homopolymer formed of the at least one monoethylenically unsaturated acid group-containing monomer, a hyperbranched polymer, and combinations thereof.
20. The method of claim 12 , further including, prior to the intra-fiber crosslinking, at least partially neutralizing the grafted polymer side chains by treating the grafted cellulosic material with an alkaline solution.