Cyclic ester dual cure resins for additive manufacturing
Disclosed herein are methods of forming a three-dimensional object having a biodegradable or bioerodible polymer or copolymer. In some embodiments, the methods include providing a dual cure resin with a photoinitiator, monomers and/or prepolymers that are polymerizable by exposure to actinic radiation or light, at least one cyclic ester, a ring-opening polymerization initiator, and a ring-opening polymerization catalyst. Resins useful for carrying out such methods, and products produced from such methods, are also described.
1. A cyclic ester dual cure resin composition comprising:
(i) a photoinitiator;
(ii) monomers and/or prepolymers that are polymerizable by exposure to actinic radiation or light;
(iii) optionally, a light absorbing pigment or dye;
(iv) at least one cyclic ester;
(v) a ring-opening polymerization initiator;
(vi) a ring-opening polymerization catalyst;
(vii) optionally a diluent; and
(viii) optionally a filler.
2. The cyclic ester dual cure resin composition of claim 1 , wherein said at least one cyclic ester is selected from the group consisting of lactides, lactones, cyclic carbonates, and combinations thereof.
3. The cyclic ester dual cure resin composition of claim 1 , wherein said initiator is selected from the group consisting of alcohols, trialkyl borates, trialkoxy borates, and tris(trimethylsilyl) borate.
4. The cyclic ester dual cure resin composition of claim 1 , wherein said catalyst is selected from the group consisting of Tin(II) octoate, metal carboxylates, metal acetylacetonate, dibutyl tin(IV) dilaurate, organophosphoric acids, basic organocatalysts, tertiary amines, phosphines, N-heterocyclic carbenes (NHCs), and catalyst pairs based on bifunctional organocatalysis with thiourea-tertiary amines.
5. The cyclic ester dual cure resin composition of claim 1 , wherein said monomers and/or prepolymers polymerizable by exposure to actinic radiation or light comprise reactive end groups selected from the group consisting of acrylates, methacrylates, α-olefins, N-vinyls, acrylamides, methacrylamides, styrenics, epoxides, thiols, 1,3-dienes, vinyl halides, acrylonitriles, vinyl esters, maleimides, and vinyl ethers.
6. The cyclic ester dual cure resin composition of claim 1 , wherein said light absorbing pigment or dye is present and is:
(i) titanium dioxide,
(ii) carbon black, and/or
(iii) an organic ultraviolet light absorber.
7. The cyclic ester dual cure resin composition of claim 1 , wherein said diluent is present and comprises an acrylate, a methacrylate, a styrene, an acrylic acid, a vinylamide, a vinyl ether, a vinyl ester, polymers containing any one or more of the foregoing, or a combination of two or more of the foregoing.
8. The cyclic ester dual cure resin composition of claim 1 , wherein said polymerizable liquid comprises:
(i) from 0.1 to 4 percent by weight of said photoinitiator;
(ii) from 10 to 90 percent by weight of said monomers and/or prepolymers that are polymerizable by exposure to actinic radiation or light;
(iii) from 0.001 to 5 percent by weight of said light absorbing pigment or dye when present;
(iv) from 10 to 90 percent by weight of said at least one cyclic ester;
(v) from 0.001 to 8 percent by weight of said ring-opening polymerization initiator;
(vi) from 0.001 to 8 percent by weight of said ring-opening polymerization catalyst;
(vii) from 1 to 40 percent by weight of said diluent when present; and
(viii) from 1 to 50 percent by weight of said filler when present.
9. The cyclic ester dual cure resin composition of claim 1 , wherein said at least one cyclic ester comprises a lactide.
10. The cyclic ester dual cure resin composition of claim 9 , wherein the lactide comprises a lactide of Formula Ia or Formula Ib:
wherein:
each R is independently selected from H, hydroxyl, C1-C20 alkyl, C1-C20 allyl, C1-C20 alkoxy, C1-C26 arylalkyl, and C1-C26 arylalkoxy; and
n is 1, 2, or 3.
11. The cyclic ester dual cure resin composition of claim 1 , wherein said at least one cyclic ester comprises a lactone.
12. The cyclic ester dual cure resin composition of claim 11 , wherein the lactone is a six-membered ring lactone or a seven-membered ring lactone.
13. The cyclic ester dual cure resin composition of claim 1 , wherein said at least one cyclic ester comprises a cyclic carbonate.
14. The cyclic ester dual cure resin composition of claim 13 , wherein said cyclic carbonate is a five-membered ring cyclic carbonate or a six-membered ring cyclic carbonate.
15. The cyclic ester dual cure resin composition of claim 1 , wherein said at least one cyclic ester comprises two or three different cyclic esters.
16. The cyclic ester dual cure resin composition of claim 1 , wherein said composition comprises from 10 to 90 percent by weight of said at least one cyclic ester.