Bearing constituent member, method of manufacturing bearing constituent member, and rolling bearing
View Patent ↗A bearing constituent member includes a base material including steel and a carbonitrided layer that is a surface layer on the steel, the steel including 0.3 to 0.45 mass % of carbon, 0.5 mass % or lower of silicon, 0.4 to 1.5 mass % of manganese, 0.3 to 2 mass % of chromium, 0.1 to 0.35 mass % of molybdenum, 0.2 to 0.4 mass % of vanadium, and a remainder of iron and unavoidable impurities. Surface Vickers hardness at a position at a depth of 50 μm from a surface of a rolling sliding surface is 700 to 800, internal hardness is 550 to 690 in terms of Vickers hardness, and an amount of residual austenite in a range from the surface to a depth of 10 μm is at least 30 vol %.
1. A bearing constituent member having a rolling sliding surface that relatively makes contact with a counterpart member, the contact including at least one of rolling contact and sliding contact, the bearing constituent member comprising
a base material including steel and a carbonitrided layer that is a surface layer on the steel, the steel including 0.3 to 0.45 mass % of carbon, 0.5 mass % or lower of silicon, 0.4 to 1.5 mass % of manganese, 0.3 to 2 mass % of chromium, 0.1 to 0.35 mass % of molybdenum, 0.2 to 0.4 mass % of vanadium, and a remainder of iron and unavoidable impurities, wherein
surface Vickers hardness at a position at a depth of 50 μm from a surface of the rolling sliding surface is 700 to 800,
internal hardness is 550 to 690 in terms of Vickers hardness, and
an amount of residual austenite in a range from the surface to a depth of 10 μm is at least 30 vol %.
2. A rolling bearing comprising:
an outer ring that has a raceway surface on an inner periphery thereof;
an inner ring that has a raceway surface on an outer periphery thereof; and
a plurality of rolling elements disposed between the raceway surface of the outer ring and the raceway surface of the inner ring, wherein
at least one of the outer ring, the inner ring, and the plurality of rolling elements is constituted by the bearing constituent member according to claim 1 .
3. The rolling bearing according to claim 2 , wherein the rolling bearing is a medium-sized tapered roller bearing.
4. A method of manufacturing the bearing constituent member according to claim 1 , the method comprising:
a carbonitriding quenching step of performing a carbonitriding quenching treatment of heating and holding a formed material at 830° C. to 930° C. in a carbonitriding atmosphere having a carbon potential of 1 to 1.3 and an ammonia concentration of 1 to 6 vol % and then quenching the base material, the formed material being formed of steel including 0.3 to 0.45 mass % of carbon, 0.5 mass % or lower of silicon, 0.4 to 1.5 mass % of manganese, 0.3 to 2 mass % of chromium, 0.1 to 0.35 mass % of molybdenum, 0.2 to 0.4 mass % of vanadium, and a remainder of iron and unavoidable impurities; and
a tempering step of tempering the formed material that has undergone the carbonitriding quenching step, at 150° C. to 250° C.