Sintered alloy and manufacturing method thereof
View Patent ↗A sintered alloy includes, in percentage by mass, Cr: 11.75 to 39.98, Ni: 5.58 to 24.98, Si: 0.16 to 2.54, P: 0.1 to 1.5, C: 0.58 to 3.62 and the balance of Fe plus unavoidable impurities; a phase A containing precipitated metallic carbides with an average particle diameter of 10 to 50 μm; and a phase B containing precipitated metallic carbides with an average particle diameter of 10 μm or less, wherein the phase A is randomly dispersed in the phase B and the average particle diameter DA of the precipitated metallic carbides in the phase A is larger than the average particle diameter DB of the precipitated metallic carbides of the phase B.
1. A method for manufacturing a sintered alloy, comprising:
preparing an iron alloy powder A consisting of, in percentage by mass, Cr: 25 to 45, Ni: 5 to 15, Si: 1.0 to 3.0, C: 1.5 to 4.0 and the balance of Fe plus unavoidable impurities;
preparing an iron alloy powder B consisting of, in percentage by mass, Cr: 12 to 25, Ni: 5 to 15 and the balance of Fe plus unavoidable impurities;
preparing an iron-phosphorus powder consisting of, in percentage by mass, P:10 to 30 and the balance of Fe plus unavoidable impurities, a nickel powder and a graphite powder;
mixing the iron alloy powder A with the iron alloy powder B so that a ratio of the iron alloy powder A to a total of the iron alloy powder A and the iron alloy powder B is within a range of 20 to 80 mass %, and adding the iron-phosphorus powder within a range of 1.0 to 5.0 mass %, the nickel powder within a range of 1 to 12 mass % and the graphite powder within a range of 0.5 to 2.5 mass % to form a raw material powder;
pressing and sintering the raw material powder to obtain the sintered alloy.
2. The method as set forth in claim 1 ,
wherein a maximum particle diameter of the iron alloy powder A is set within a range of 300 μm or less.
3. The method as set forth in claim 1 ,
wherein a maximum particle diameter of the nickel powder is set within a range of 74 μm or less.
4. The method as set forth in claim 1 , further comprising:
adding 5 mass % or less of at least one selected from the group consisting of Mo, V, W, Nb and Ti to either or both of the iron alloy powder A and the iron alloy powder B.
5. The method as set forth in claim 1 ,
wherein a sintering temperature is set within a range of 1000 to 1200° C.
6. The method as set forth in claim 1 ,
wherein the iron alloy powder A contains carbon within a range of 2.0 to 4.0 mass %.
7. The method as set forth in claim 1 ,
wherein the chromium content of the iron alloy powder A is larger than the chromium content of the iron alloy powder B.
8. The method as set forth in claim 1 ,
wherein the iron alloy powder A has carbides containing chromium.