Polyethylene terephthalate depolymerization
The present invention relates to the depolymerization of polymers and the recovery of the starting materials used for the production of the polymer. The present invention also relates to the depolymerization of polyethylene terephthalate (PET) and the recovery of terephthalic acid and ethylene glycol.
1. A process for depolymerizing polyethylene terephthalate, comprising admixing the polyethylene terephthalate with a mixture comprising:
(i) a non-polar solvent; and
(ii) a mixture of an alcohol and a hydroxide;
wherein the admixing is continued for a sufficient time to depolymerize at least a portion of the polyethylene terephthalate; and
wherein the process is performed without applying external heat.
2. The process of claim 1 , wherein the mixture of the alcohol and the hydroxide is added to the polyethylene terephthalate simultaneously with the non-polar solvent.
3. The process of claim 1 , wherein the ratio of the non-polar solvent to alcohol is about 1:10 to about 1:50 (v:v).
4. The process of claim 1 , wherein the polyethylene terephthalate is admixed with the non-polar solvent, the hydroxide, and the alcohol for about 0 h to about 5 h.
5. The process of claim 4 , wherein the polyethylene terephthalate is admixed with the non-polar solvent, the hydroxide, and the alcohol at atmospheric pressure.
6. The process of claim 1 , wherein the non-polar solvent is a halogenated solvent.
7. The process of claim 1 , wherein the alcohol is a linear C 1 -C 4 alcohol.
8. The process of claim 1 , wherein the hydroxide is selected from the group consisting of an alkali metal hydroxide, an alkaline earth metal hydroxide, an ammonium hydroxide, and a combination thereof.
9. The process of claim 1 , wherein the polyethylene terephthalate is in the form of waste material.
10. The process of claim 9 , wherein the waste material further comprises debris that does not include polymers comprising an ester functionality.
11. The process of claim 10 , wherein the debris comprises at least one of bottle caps, glue, paper, residual liquid, or dirt.
12. The process of claim 1 , wherein the polyethylene terephthalate is depolymerized to form terephthalic acid or a salt thereof and ethylene glycol.
13. The process of claim 12 , wherein the terephthalic acid or a salt thereof contains less than about 3% of an impurity (w/w).
14. The process of claim 13 , wherein the impurity comprises at least one of isophthalic acid, phthalic acid, 4-methylbenzoic acid, 4-formylbenzoic acid, or metals.
15. A process for depolymerizing polyethylene terephthalate, comprising admixing the polyethylene terephthalate with a mixture comprising:
(i) about 3 to about 5% (vol.) of a non-polar solvent, wherein the non-polar solvent is a halogenated solvent;
(ii) about 95 to about 97% (vol.) of a linear C 1 -C 4 alcohol; and
(iii) a hydroxide;
wherein the admixing is continued for about 1 h; and
wherein the process is performed without applying external heat.
16. The process of claim 15 , wherein the polyethylene terephthalate is depolymerized to form terephthalic acid or a salt thereof and ethylene glycol.
17. The process of claim 16 , wherein the terephthalic acid or salt thereof contains less than about 3% of an impurity (w/w).
18. The process of claim 17 , wherein the impurity comprises at least one of isophthalic acid, phthalic acid, 4-methylbenzoic acid, 4-formylbenzoic acid, or metals.