Anti-fouling surface coating materials
An anti-fouling (anti-pollution) coating material and a method of manufacturing a coating film are provided herein. The anti-fouling coating material has characteristics such as, but not limited to, an anti-fouling property, water repellency, oil repellency, and improved adhesion to a base material such as a lens. The anti-fouling coating material includes (a) a base material, (b) a low-reflectivity coating layer having a multilayer structure in which a silicon dioxide (SiO 2 )-containing layer and a titanium dioxide (TiO 2 )-containing layer are alternately stacked, (c) an anti-fouling coating layer that is formed on the low-reflectivity coating layer and includes an organic/inorganic composite material in which a silicon compound and a fluorine compound are linked to each other, and (d) an adhesion improving layer interposed between the base material and the low-reflectivity coating layer. The anti-fouling coating material is not readily detached to the surface of the base material such as a lens due to its superior adhesivity. Thus, the anti-fouling coating material can stably exert water repellency and oil repellency for a long time.
1. An anti-fouling coating material comprising:
a base material;
a reflectivity coating layer being formed on the base material and having a multilayer structure in which a silicon dioxide (SiO 2 )-containing layer and a titanium dioxide (TiO 2 )-containing layer are alternately stacked;
an anti-fouling coating layer being formed on the reflectivity coating layer and including an organic/inorganic composite material in which a silicon compound and a fluorine compound are linked to each other; and
an adhesion improving layer interposed between the base material and the reflectivity coating layer.
2. The anti-fouling coating material according to claim 1 , wherein the reflectivity coating layer comprises the silicon dioxide (SiO 2 )-containing layer disposed on a surface of the reflectivity coating layer contacting the anti-fouling coating layer.
3. The anti-fouling coating material according to claim 1 , wherein the silicon compound is selected from a group consisting of octadecyltrimethoxy silane, octyltrimethoxy silane, methyltrimethoxy silane, ethyltrimethoxy silane, ethyltriethoxy silane, propyltrimethoxy silane, n-propyltriethoxy silane, isopropyltriethoxy silane, n-butyltrimethoxy silane, isobutyltrimethoxy silane, phenyltrimethoxy silane, N-(2-aminoethyl)-3-aminopropyltrimethoxy silane, 3-mercaptopropyltrimethoxy silane, 3-mercaptopropyltriethoxy silane, 3-aminopropyltriethoxy silane, 3-aminopropyltrimethoxy silane, 3-(meth)acryloxypropyltrimethoxy silane, 3-(meth)acryloxypropyltriethoxy silane, phenylaminopropyltrimethoxy silane, vinyltriethyloxy silane, vinyltrimethoxy silane, allyltrimethoxy silane and a combination thereof.
4. The anti-fouling coating material according to claim 1 , wherein the fluorine compound is selected from a group consisting of perfluoropolyether (PFPE), polytetrafluoroethylene (PTFE), fluorinated ethylene propylene copolymer (FEP), a perfluoroalkyl vinyl ether copolymer, and a combination thereof.
5. The anti-fouling coating material according to claim 1 , wherein the anti-fouling coating layer has a fluorine content of from about 10 to 50 wt %.
6. The anti-fouling coating material according to claim 1 , wherein the anti-fouling coating layer has a thickness of from about 5 to 200 nm.
7. The anti-fouling coating material according to claim 1 , wherein the anti-fouling coating layer has a water contact angle of from about 100 to 150 degrees.
8. The anti-fouling coating material according to claim 1 , wherein the anti-fouling coating layer has a hexadecane contact angle of from about 40 to 90 degrees.
9. The anti-fouling coating material according to claim 1 , wherein the adhesion improving layer is a silica oxide film composed of silicon dioxide (SiO 2 ).
10. The anti-fouling coating material according to claim 1 , wherein the adhesion improving layer has a thickness of from about 10 to 100 nm.