Porous granules containing mixture of rubber and silica powders
Granules containing mixtures of silica powder and cross-linked rubber powder are used in the manufacture of battery separators or vehicle tires. A granule contains silica and rubber powders in proportional amounts that form a silica powder carrier within which rubber powder particles are distributed. Incorporating silica-rubber granules in the manufacturing process of polyethylene separators offers a way to limit water loss in and improve the cycle life of a deep cycle lead-acid battery. Incorporating silica-rubber granules in the manufacturing process of vehicle tires affords advantages including easier material handling, reduced production of dust, and reduction in the number of ingredients measured and added to the formulation.
1. A silica-rubber granule, comprising:
a combination including a first amount of a silica component and a second amount of a rubber component, the first amount of the silica component being greater than the second amount of the rubber component, the combination of the first and second amounts of the respective silica and rubber components comprised in a granule in which the silica component of the granule is a carrier within which the rubber component is distributed, wherein the granule comprises a compression-formed granule established by the dry combination of the first and second amounts of the respective silica and rubber components, and wherein a ratio, by weight, of the first amount of the silica component to the second amount of the rubber component is from about 4:1 to about 9:1.
2. The silica-rubber granule of claim 1 , wherein the silica component comprises a spray-dried silica component, the rubber component comprises a spray-dried rubber component, or both.
3. The silica-rubber granule of claim 2 , wherein both the spray-dried silica component and the spray-dried rubber component are spray dried individually or in combination.
4. The silica-rubber granule of claim 2 , wherein the spray-dried rubber component comprises a spray-dried rubber latex or spray-dried rubber slurry.
5. The silica-rubber granule of claim 1 , wherein the silica component comprises precipitated silica, precipitated silica derivatives, fumed silica, fumed silica derivatives, or mixtures thereof.
6. The silica-rubber granule of claim 5 , wherein the precipitated silica comprises amorphous precipitated silica.
7. The silica-rubber granule of claim 6 , wherein the amorphous precipitated silica has a surface area of about 50 m 2 /g to about 350 m 2 /g.
8. The silica-rubber granule of claim 1 , wherein the silica component comprises a silica particle with a silane coupling agent attached to a surface of the silica particle.
9. The silica-rubber granule of claim 1 , wherein the rubber component comprises a cross-linked rubber powder.
10. The silica-rubber granule of claim 1 , further comprising a third amount of an additive.
11. The silica-rubber granule of claim 1 , wherein the granule has a size of about 100 microns to about 5 mm.
12. A vehicle tire or a battery separator manufactured from a formulation comprising the silica-rubber granule of claim 1 .
13. A method of manufacturing a battery separator, the method comprising:
mixing polyethylene with the silica-rubber granule of claim 1 and a plasticizer to form a mixture;
heating the mixture above the melting point of the polyethylene; and
extruding the heated mixture through a die.
14. The method of claim 13 , wherein the polyethylene comprises ultra-high molecular weight polyethylene powder.
15. The method of claim 13 , wherein the plasticizer comprises a process oil.
16. The method of claim 13 , further comprising using spray-drying to form the silica component, the rubber component, or both of the silica-rubber granule, wherein in the case of both, then both the silica component and the rubber component are either formed individually or in combination.
17. A silica-rubber granule, comprising:
a combination including a first amount of a silica component and a second amount of a rubber component, the first amount of the silica component being greater than the second amount of the rubber component, the combination of the first and second amounts of the respective silica and rubber components comprised in a granule in which the silica component of the granule is a carrier within which the rubber component is distributed, wherein a ratio, by weight, of the first amount of the silica component to the second amount of the rubber component is from about 4:1 to about 9:1, wherein the granule comprises a compression-formed granule established by the combination of the first and second amounts of the respective silica and rubber components, and wherein the rubber component comprises a previously cross-linked rubber powder.
18. A silica-rubber granule, comprising:
a combination including a first amount of a silica component and a second amount of a rubber component, the first amount of the silica component being greater than the second amount of the rubber component, the combination of the first and second amounts of the respective silica and rubber components comprised in a compression-formed granule in which the silica component of the granule is a carrier within which the rubber component is distributed, wherein a ratio, by weight, of the first amount of the silica component to the second amount of the rubber component is from about 4:1 to about 9:1, wherein the precipitated silica comprises amorphous precipitated silica, and wherein the amorphous precipitated silica has a surface area of about 50 m 2 /g to about 350 m 2 /g.