COVER GLASS AND PROCESS FOR PRODUCING THE SAME
A cover glass includes a glass substrate and an antireflection film disposed on at least one of main surfaces of the glass substrate, and the at least one of main surfaces of the glass substrate has one or more cracks formed therein, the crack(s) each having a length of 5 μm or less, and a difference Δa* in a* value between any two points within a surface of the cover glass on the side where the antireflection film has been disposed and a difference Δb* in b* value between any two points within the surface of the cover glass on the side where the antireflection film has been disposed satisfy the following expression: √{(Δ a *) 2 +(Δ b *) 2 }≦4.
1 . A cover glass comprising a glass substrate and an antireflection film disposed on at least one of main surfaces of the glass substrate, wherein
the at least one of main surfaces of the glass substrate has one or more cracks formed therein, the crack(s) each having a length of 5 μm or less, and
a difference Δa* in a* value between any two points within a surface of the cover glass on the side where the antireflection film has been disposed and a difference Δb* in b* value between any two points within the surface of the cover glass on the side where the antireflection film has been disposed satisfy the following expression (1).
√{(Δ a *) 2 +(Δ b *) 2 }≦4 (1)
2 . The cover glass according to claim 1 , wherein the Δa* and the Δb* are determined by selecting any square portion of 10 cm 2 as a measuring range from the surface of the cover glass on the side where the antireflection film has been disposed, dividing the measuring range into 11×11 equal portions, examining all 100 intersections of equally dividing lines for a* values and b* values, determining a maximum value a* max of the a* values, a minimum value a* min of the a* values, a maximum value b* max of the b* values, and a minimum value b* min of the b* values, from the a* values and b* values, and taking a difference (a* max −a* min ) between the a* max and the a* min as the Δa* and a difference (b* max −b* min ) between the b* max and the b* min as the Δb*.
3 . The cover glass according to claim 1 , wherein the antireflection film is a laminate comprising one or more layers containing niobium and one or more layers containing silicon.
4 . The cover glass according to claim 2 , wherein the antireflection film is a laminate comprising one or more layers containing niobium and one or more layers containing silicon.
5 . The cover glass according to claim 1 , which has a luminous reflectance of 2% or less.
6 . The cover glass according to claim 1 , further comprising an antifouling film disposed on the antireflection film, wherein a contact angle of water on a surface of the cover glass on the side where the antifouling film has been disposed is 90° or larger.
7 . A process for producing a cover glass, the process comprising:
an acid treatment step of subjecting surfaces of a glass substrate to an acid treatment;
an alkali treatment step of subjecting the glass substrate which has been acid-treated to an alkali treatment; and
a step of depositing a antireflection film on a main surface of the glass substrate which has been alkali-treated.
8 . The process for producing a cover glass according to claim 7 , wherein a glass substrate which has been chemically strengthened is subjected to the acid treatment in the acid treatment step.