Method for solution heat treating with pressure
A method of heat treating high pressure die cast objects using pressure is disclosed. A high pressure die cast object is obtained and solution heat treated to above 700° F. for at least 2 hours at pressures between 0.5 and 35 KSI or at any pressure or range of pressures therebetween. This method of solution heat treatment with pressure reduces and/or eliminates blistered defects on the high pressure die cast object. The method of heat treating by solution heat treatment with pressure also allows an increase of yield strength and corresponding weight reduction upon redesign or substantially larger safety factors for the cast object.
1. A method of heat treating a high pressure die cast aluminum alloy object, the method comprising: obtaining a high pressure die cast aluminum alloy object; and solution heat treating the high pressure die cast aluminum alloy object above 700° F. while applying pressure between 2.5 and 10 KSI for 2 to 8 hours in a solution heat treatment vessel, and quenching the high pressure die cast aluminum alloy object after removing the object from the solution heat treatment vessel; wherein the step of solution heat treating eliminates blistering defects on the high pressure die cast.
2. The method of claim 1 wherein the step of solution heat treating comprises applying pressure between 2.5 and 5 KSI and the method further comprises subsequently quenching the cast object and artificially aging the cast object to effect a T6 heat treatment.
3. The method of claim 1 wherein the step of solution heat treating comprises solution heat treating the high pressure die cast object between 700° F. and 1200° F.
4. The method of claim 1 wherein the step of solution heat treating comprises solution heat treating the high pressure die cast object at 1000° F.
5. The method of claim 1 wherein the step of solution heat treating comprises applying pressure between 2.5 and 5 KSI, and wherein the step of solution heat treating eliminates blistering defects on the high pressure die cast object.
6. The method of claim 1 wherein the step of solution heat treating comprises solution heat treating the high pressure die cast object for 4 to 6 hours.
7. The method of claim 1 wherein the method of heat treating further comprises the step of artificially aging the high pressure die cast object.
8. A method of heat treating a high pressure die cast aluminum alloy object, the method comprising: casting an aluminum alloy object with high pressure die casting equipment; removing the cast aluminum alloy object from the high pressure die casting equipment; placing the cast aluminum alloy object into a pressure vessel, the pressure vessel including a heating element; solution heat treating the cast aluminum alloy object above 700° F. while applying pressure between 2.5 and 10 KSI for 2 to 8 hours; removing the cast object from the pressure vessel; and quenching the die cast aluminum alloy object after removing the object from the pressure vessel, wherein the step of solution heat treating reduces blistering defects on the die cast aluminum alloy object.
9. The method of claim 8 wherein the step of solution heat treating comprises applying pressure between 2.5 and 5 KSI and the method further comprises subsequently quenching the cast object and artificially aging the cast object to effect a T6 heat treatment.
10. The method of claim 8 wherein the step of solution heat treating comprises solution heat treating the cast aluminum alloy object between 700° F. and 1200° F.
11. The method of claim 8 wherein the step of solution heat treating comprises solution heat treating the cast aluminum alloy object at 1000° F.
12. The method of claim 8 wherein the step of solution heat treating comprises applying pressure between 2.5 and 5 KSI, and wherein the step of solution heat treating eliminates blistering defects on the die cast aluminum alloy object.
13. The method of claim 8 wherein the step of solution heat treating comprises solution heat treating the cast aluminum alloy object for 4 to 6 hours.
14. The method of claim 8 wherein the method of heat treating further comprises the step of artificially aging the cast aluminum alloy object.