6xxx aluminum alloys, and methods of making the same
New 6xxx aluminum alloys having an improved combination of properties are disclosed. Generally, the new 6xxx aluminum alloys contain 1.00-1.45 wt. % Si, 0.32-0.51 wt. % Mg, wherein a ratio of wt. % Si to wt. % Mg is in the range of from 2.0:1 (Si:Mg) to 4.5:1 (Si:Mg), 0.12-0.44 wt. % Cu, 0.08-0.19 wt. % Fe, 0.02-0.30 wt. % Mn, 0.01-0.06 wt. % Cr, 0.01-0.14 wt. % Ti, and ≤0.25 wt. % Zn, the balance being aluminum and impurities, wherein the aluminum alloy includes ≤0.05 wt. % of any one impurity, and wherein the aluminum alloy includes ≤0.15 in total of all impurities.
1. An aluminum alloy consisting essentially of:
1.00-1.45 wt. % Si;
0.32-0.51 wt. % Mg;
wherein a ratio of wt. % Si to wt. % Mg is in the range of from 2.0:1 (Si:Mg) to 4.5:1 (Si:Mg);
0.12-0.44 wt. % Cu;
0.08-0.30 wt. % Fe;
0.02-0.09 wt. % Mn;
0.01-0.06 wt. % Cr;
0.01-0.14 wt. % Ti;
≤0.25 wt. % Zn;
the balance being aluminum and impurities, wherein the aluminum alloy includes ≤0.05 wt. % of any one impurity, and wherein the aluminum alloy includes ≤0.15 in total of all impurities;
wherein the aluminium alloy realizes an improved combination of strength, formability and corrosion resistance;
wherein the strength is at least one of:
(i) a tensile yield strength (LT) of from 100 to 170 MPa in a naturally aged condition; and
(ii) a tensile yield strength (LT) of from 160 to 330 MPa in the artificially aged condition;
wherein the formability is an FLD o of from 28.0 to 33.0 (Engr %) at a gauge of 1.0 mm when measured in accordance with ISO 12004-2:2008 standard, wherein the ISO standard is modified such that fractures more than 15% of the punch diameter away from the apex of the dome are counted as valid;
wherein the corrosion resistance is a depth of attack of not greater than 350 microns in near peak-aged condition when tested in accordance with ISO standard 11846(1995) (Method B), wherein the near peak-aged condition is within 10% of peak strength.
2. The aluminum alloy of claim 1 , having from 1.03 wt. % to 1.40 wt. % Si.
3. The aluminum alloy of claim 1 , having from 1.09 wt. % to 1.30 wt. % Si.
4. The aluminum alloy of claim 1 , having from 0.32 wt. % to 0.51 wt. % Mg.
5. The aluminum alloy of claim 1 , having from 0.35 wt. % to 0.47 wt. % Mg.
6. The aluminum alloy of claim 1 , wherein the ratio of wt. % Si to wt. % Mg is in the range of from 2.10:1 to 4.25 (Si:Mg).
7. The aluminum alloy of claim 1 , wherein the ratio of wt. % Si to wt. % Mg is in the range of from 2.40:1 to 3.60 (Si:Mg).
8. The aluminum alloy of claim 1 , having from 0.12 wt. % to 0.25 wt. % Cu.
9. The aluminum alloy of claim 1 , having from 0.15 wt. % to 0.20 wt. % Cu.
10. The aluminum alloy of claim 1 , having from 0.27 wt. % to 0.40 wt. % Cu.
11. The aluminum alloy of claim 1 , having from 0.06 to 0.14 wt. % Ti.
12. The aluminum alloy of claim 1 , having from 0.08 to 0.12 wt. % Ti.
13. The aluminum alloy of claim 1 , having not greater than 0.03 wt. % Zn.