Methods for Synthesizing Graphene from a Lignin Source
Processes, methods, and compositions for synthesizing carbon-based materials are provided. The method of synthesizing carbon-based materials includes providing precursors, forming carbon-encapsulated metal structures from the precursors, and forming nano-shell structure-based graphene materials from the carbon-encapsulated metal structures. The precursors are formed from a biomass and a catalyst, and may be pretreated prior to the forming of the carbon-encapsulated metal structures.
1 . A method of synthesizing carbon-based materials, the method comprising:
providing precursors;
forming carbon-encapsulated metal structures from the precursors; and
forming nano-shell structure-based graphene materials from the carbon-encapsulated metal structures.
2 . The method of claim 1 , wherein providing the precursors comprises preparing the precursors.
3 . The method of claim 2 , wherein preparing the precursors comprises mixing a biomass and a catalyst.
4 . The method of claim 3 , wherein the biomass is selected from the group consisting of kraft lignin, organosolv lignin, lignosulfonates, hydrolytic lignin, black liquor, and combinations thereof.
5 . The method of claim 3 , wherein the biomass is selected from the group consisting of woody biomass and its derivatives, wood chips, wood char, wood-based chars, pyrolysis char, starch, wood-derived sugars, active carbon, carbon black, and combinations thereof.
6 . The method of claim 3 , wherein the biomass is dispersed in a solvent selected from the group consisting of water, ethanol, acetone, 1,3-dioxane, 1,4-dioxane, tetrahydrofuran, and combinations thereof.
7 . The method of claim 3 , wherein the catalyst is selected from the group consisting of a metal catalyst, a bi-metallic catalyst, a tri-metallic catalyst, a tetra-metallic catalyst, and any other multi-metal catalyst.
8 . The method of claim 7 , wherein the metal catalyst is selected from the group consisting of transition metals, salts thereof, oxides thereof, and combinations thereof.
9 . The method of claim 7 , wherein the metal catalyst is a combination of metals selected from the group consisting of Fe, Cu, Ni, Co, Mo, W, salts thereof, oxides thereof, and combinations thereof.
10 . The method of claim 3 , wherein mixing the biomass and the catalyst includes mixing between 2.5% and 30% by weight catalyst with between 70% and 97.5% by weight biomass.
11 . The method of claim 3 , wherein mixing the biomass and the catalyst forms a catalyst-impregnated biomass.
12 . The method of claim 1 , wherein forming the carbon-encapsulated metal structures comprises thermally treating the precursors.
13 . The method of claim 1 , wherein forming nano-shell structure-based graphene materials includes opening the carbon-encapsulated metal structures to form shell-like structures, then welding and reconstructing the shell-like structures to form the nano-shell structure-based graphene materials.
14 . The method of claim 13 , wherein welding and reconstructing the shell-like structures comprises application of a welding reagent gas under high temperature.
15 . The method of claim 14 , wherein the welding reagent gas is selected from the group consisting of light hydrocarbons, argon, hydrogen, natural gas, other carbonaceous gases, and combinations thereof.
16 . The method of claim 14 , wherein the high temperature includes a temperature of between 500° C. and 1,500° C.
17 . The method of claim 1 , further comprising pretreating the precursor prior to forming the carbon-encapsulated metal structures.
18 . The method of claim 17 , wherein the pretreating is selected from the group consisting of pre-decomposing the precursor, grinding the precursor, and a combination thereof.
19 . The method of claim 1 , wherein the nano-shell structure-based graphene materials comprise multi-layer graphene-based materials selected from the group consisting of nano-graphene shell connected chains, graphene nanoplatelets, fluffy graphene, flat graphene sheets, curved graphene sheets, graphene sponges, graphene-encapsulated metal, metal carbide nanoparticles, graphene strips with a common metal joint, and combinations thereof.
20 . The method of claim 1 , further comprising post-treating the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
21 . The method of claim 1 , further comprising purifying the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
22 . The method of claim 20 , further comprising purifying the graphene materials with water, steam carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
23 . A method of synthesizing carbon-based materials, the method comprising:
preparing precursors from a biomass and a catalyst;
forming carbon-encapsulated metal structures from the precursors, the forming of the carbon-encapsulated metal structures including thermally treating the precursors; and
forming nano-shell structure-based graphene materials from the carbon-encapsulated metal structures, the forming of the nano-shell structure based graphene materials including opening the carbon-encapsulated metal structures to form shell-like structures, then welding and reconstructing the shell-like structures to form the nano-shell structure-based graphene materials;
wherein the biomass is selected from the group consisting of kraft lignin, organosolv lignin, lignosulfonates, black liquor, hydrolytic lignin, woody biomass and its derivatives, wood ships, wood char, wood-based chars, pyrolysis char, starch, wood-derived sugars, active carbon, carbon black, and combinations thereof; and
wherein the catalyst is at least one transition metal.
24 . The method of claim 23 , wherein mixing preparing the precursors includes forming a catalyst-impregnated biomass.
25 . The method of claim 23 , further comprising post-treating the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
26 . The method of claim 23 , further comprising purifying the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
27 . The method of claim 25 , further comprising purifying the graphene materials with water, steam carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
28 . A method of synthesizing carbon-based materials, the method comprising:
preparing precursors from a kraft lignin and a transition metal catalyst;
pretreating the precursors;
forming carbon-encapsulated metal structures from the precursors, the forming of the carbon-encapsulated metal structures including thermally treating the precursors; and
forming nano-shell structure-based graphene materials from the carbon-encapsulated metal structures, the forming of the nano-shell structure based graphene materials including opening the carbon-encapsulated metal structures to form shell-like structures, then welding and reconstructing the shell-like structures to form the nano-shell structure-based graphene materials.
29 . The method of claim 28 , further comprising post-treating the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
30 . The method of claim 28 , further comprising purifying the graphene materials with water, steam, carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
31 . The method of claim 29 , further comprising purifying the graphene materials with water, steam carbon dioxide, hydrogen sulfide, carbon disulfide, ammonia, a basic solution, or an acid solution.
32 . A method of synthesizing carbon-encapsulated metal structures, the method comprising:
preparing precursors from a biomass and a catalyst;
optionally pretreating the precursors; and
thermally treating the precursors to form carbon-encapsulated metal structures.