Extruded flexible flat cable
View Patent ↗An extruded flexible flat cable, which has a superior formability, flexibility, adhesiveness, and fire-retardancy, with a low manufacturing cost, is adapted for sliding door of a motor vehicle and also other parts, and has a conductor covered with an insulation layer extrude-formed with an extrusion molding method, and the insulation layer formed from a fire-retardant resin composition containing a modified polybutylene terephthalate and a fire-retardant additive, where the fire-retardant resin composition has a melting point of 170-215 degrees C. measured in reference to JIS K7121 with a differential thermal analysis at a rate of temperature increase of 10 degrees C. per minute.
1. An extruded flexible flat cable having a conductor covered with an insulation layer extrude-formed with an extrusion molding method,
the insulation layer being formed from a fire-retardant resin composition containing a resin composition and a fire-retardant additive,
the fire-retardant resin composition having a melting point of 170-215 degrees C. measured with a differential thermal analysis at a rate of temperature increase of 10 degrees C. per minute,
wherein a resin component of the resin composition consists of a modified polybutylene terephthalate,
wherein the fire-retardant additive consists of organic/inorganic acid, and
wherein the modified polybutylene terephthalate is a copolymer obtained by copolymerizing a terephthalic acid or its reaction derivative, 1,4-butanediol and a monomer copolymerizable with the 1,4-butanediol.
2. The extruded flexible flat cable as claimed in claim 1 , wherein the insulation layer around the conductor is formed with an extrusion molding machine by extruding a single layer of the fire-retardant resin composition around the conductor supplied to a cross head of the extrusion molding machine.
3. The extruded flexible flat cable as claimed in claim 2 , wherein the conductor has a thickness of at least 0.1 mm and the flat cable has a flexion cycle of at least 7*10 4 measured with a flexural fatigue tester at a flexion radius of R=10 and at a temperature of 25 ±3 degrees C.
4. The extruded flexible flat cable as claimed in claim 3 , wherein the extruded flexible flat cable is adapted for electrical connection between a movable portion and a stationary portion of a motor vehicle.
5. The extruded flexible flat cable as claimed in claim 2 , wherein the extruded flexible flat cable is adapted for electrical connection between a movable portion and a stationary portion of a motor vehicle.
6. The extruded flexible flat cable as claimed in claim 1 , wherein the extruded flexible flat cable is adapted for electrical connection between a movable portion and a stationary portion of a motor vehicle.
7. The extruded flexible flat cable as claimed in claim 1 , wherein the flexible flat cable has a flame retardancy such that a flame disappears within 30 seconds after the flexible flat cable is exposed to a flame for 10 seconds.
8. The extruded flexible flat cable as claimed in claim 1 , wherein the modified polybutylene terephthalate is formed of one of:
I) a dicarboxylic acid containing terephthalic acid and isophthalic acid with a mole ratio of 87.5/12.5, and 1,4-butanediol as a diol component;
II) a dicarboxylic acid containing terephthalic acid and isophthalic acid with the mole ratio of 75/25, and 1,4-butanediol as a diol component; and
III) a combination of I and II in a 1-to-1 weight ratio.
9. The extruded flexible flat cable as claimed in claim 1 , wherein the extruded flexible flat cable has a peeling strength of at least 40 MPa at 180°.
10. The extruded flexible flat cable as claimed in claim 1 , wherein the fire-retardant additive includes a salt of Ca, Mg and Al of a lower alkyl phosphinic acid.