Superhydrophobic and oleophobic coatings with low VOC binder systems

1. A coating composition for the application of superhydrophobic, or superhydrophobic and oleophobic, coatings on surfaces comprising:

a one-component waterborne polyurethane dispersion or suspension comprising one or more of a polyester urethane, a polyacrylic urethane and/or a polycarbonate urethane in water, or a water containing medium;

about 5 to about 30% by weight of hydrophobic, or superhydrophobic and oleophobic, second particles comprising one or more siloxanes, and/or one or more alkyl, haloalkyl, fluoroalkyl, or perfluoroalkyl containing moieties;

said composition optionally comprising up to about 26% by weight of third particles;

wherein said coating composition comprises less than 0.3 pounds per gallon of volatile non-exempt organic compounds;

wherein said coating composition optionally comprises first particles;

and

wherein the superhydrophobic coating resulting from the application of said composition to a surface retains its superhydrophobicity after 150-1,400 Taber abrasion cycles at a 1000 g load for a coating thickness range of 25-300 microns, and/or 100-2,500 Taber abrasion cycles at a 250 g load, using a CS10 wheel, as judged by the inability of more than 50% of the water droplets applied to the area of the coating subjected to said abrasion cycles to remain on the surface when the planar surface is inclined at 3 degrees.

2. The composition of claim 1 , wherein said composition does not comprise first particles and the superhydrophobic coating resulting from the application of said composition to a planar surface retains its superhydrophobicity after 150-800 Taber abrasion cycles at a 1,000 g load, for a thickness range of 25-75 microns, and/or 200-1,400 Taber abrasion cycles at a 250 g load for a thickness range of 25-75 microns, on a planar surface using a CS10 wheel, as judged by the inability of more than 50% of the water droplets applied to the area of the coating subjected to said abrasion cycles to remain on the surface when the planar surface is inclined at an angle of 3 degrees.

3. The composition of claim 1 , wherein said composition further comprises first particles.

4. The composition of claim 3 , wherein the first particles are selected from oxides of metalloids, metal oxides, one or more thermoplastics, one or more thermoset plastics, one or more metals, one or more glasses, and/or one or more hollow spheres.

5. The composition of claim 3 , wherein the superhydrophobic coating resulting from the application of said composition to a planar surface retains its superhydrophobicity after 100-600 Taber abrasion cycles at a 250 g load for a thickness range of 40-85 microns using a CS10 wheel, as judged by the inability of more than 50% of the water droplets applied to the area of the coating subjected to said abrasion cycles to remain on the surface when the planar surface is inclined at an angle of 3 degrees.

6. The composition of claim 1 , wherein said polyurethane suspension or dispersion comprises third particles.

7. The composition of claim 1 , wherein the composition comprises a mixture of polyacrylic urethanes and polycarbonate urethanes.

8. The composition of claim 1 , wherein said one or more alkyl, haloalkyl, fluoroalkyl, or perfluoroalkyl containing moieties are one or more alkylsilane and/or fluoroalkylsilane groups.

9. The composition of claim 8 , wherein said alkylsilane and/or fluoroalkylsilane groups result from the reaction of silica or metal oxide particles with one or more silanes selected from the group consisting of: a compound of formula I; (tridecafluoro-1,1,2,2-tetrahydrooctyl)silane; (tridecafluoro-1,1,2,2-tetrahydrooctyl)trichlorosilane; (tridecafluoro-1,1,2,2-tetrahydrooctyl)triethoxysilane; (tridecafluoro-1,1,2,2-tetrahydrooctyl)trimethoxysilane; (heptadecafluoro-1,1,2,2-tetrahydrodecyl)dimethyl(dimethylamino)silane; (heptadecafluoro-1,1,2,2-tetrahydrodecyl)tris(dimethylamino)silane; n-octadecyltrimethoxysilane; n-octyltriethoxysilane; and 3,3,4,4,5,5,6,6,6-nonafluorohexyldimethyl(dimethylamino)silane.

10. The composition of claim 9 , wherein said second particles are present from about 20% to about 30% by weight.

11. The composition of claim 9 , wherein said coating is both superhydrophobic and oleophobic.

12. The composition of claim 1 , that when dried and cured produces a surface with an arithmetic mean roughness (Ra) of less than about 20 microns.

13. The composition of claim 1 , comprising from about 30% to about 50% polyurethanes by weight.

14. The composition of claim 1 , wherein said polyurethane dispersion or suspension comprises at least one polyester urethane, polyacrylic urethane, and/or polycarbonate urethane composition that when dried and cured produces a coating that has: (a) a modulus at 100% elongation of 1300 psi or greater, and/or (b) an elongation percent at break of 150% or greater.

15. The composition of claim 1 , further comprising 0.1-10, 10-20, 20-30, 30-40, 40-50 or 50-60 g of one or more compatible solvents per 100 g of coating composition.

16. The composition of claim 15 , wherein said one or more compatible solvents are VOC-exempt solvents, and wherein said coating composition comprises less than 0.3 pounds per gallon of volatile non-exempt organic compounds.

17. The composition according to claim 16 , wherein said one or more VOC-exempt solvents comprise water.

18. A superhydrophobic and/or oleophobic coating formed by the application of the composition of claim 1 .

19. The coating of claim 18 , wherein said coating formed on a flat flexible surface can withstand being bent to a right angle around a ¼ inch cylinder greater than about 100 times without loss of hydrophobicity or oleophobicity.

20. A method of coating at least part of a surface comprising the application of a composition of claim 1 .