A rare earth bonded magnet comprises a rare earth-iron-based magnetic powder and a thermosetting resin composition. The thermosetting resin composition is obtained by blending a dicyclopentadiene type epoxy resin as a base resin and dicyandiamide as a curing agent. The dicyclopentadiene type epoxy resin includes a predetermined structure wherein an average value of a repeating unit n is 1 to 3.
1. A rare-earth bonded magnet comprising:
A rare-earth-iron-based magnetic powder comprising neodymium, iron and boron as main components; and
a thermosetting resin,
the thermosetting resin composition being obtained by blending a dicyclopentadiene type epoxy resin as a base resin and dicyandiamide as a curing agent, the dicyclopentadiene type epoxy resin including a structure represented by the following formula (1) where the average value of a repeating unit n is 1 to 3,
wherein 70% or more of the dicyclopentadiene type epoxy resin blended in the thermosetting resin is the dicyclopentadiene type epoxy resin of the structure where the respecting unit n is 1,
wherein thermal demagnetization rate after 1000 h heat exposure at 180° C. is 10% to about 12%,
the rare earth bonded magnet comprises 1 to 3 mass % of the thermosetting resin, and
a Tg (glass transition temperature) of the dicyclopentadiene type epoxy resin after reacted to the curing agent is about 160° C.
2. The rare earth bonded magnet according to claim 1 , wherein radial crushing strength is 50 MPa or higher.