Self-healing material and preparation process thereof
View Patent ↗The present application provides a self-healing material which comprises silica sol as self-healing agent encapsulated by a polymeric shell. The self-healing material may be further embedded in a concrete mixture to heal micro-cracks in concrete. A method for preparing the self-healing material is also provided.
1. A process for preparing a composite material comprising:
emulsifying a colloidal silica core in presence of a solvent and a mixture of at least two surfactants at an emulsifying speed within a range of 400-600 rpm, wherein the mixture of at least two surfactants is having a hydrophile-lipophile balance (HLB) within a range of 3.0-5.0; and
encapsulating the emulsified colloidal silica core with a polymer shell to form a plurality of microcapsules.
2. The process of claim 1 , wherein the weight percentage of silicon dioxide in the colloidal silica ranges from about 40% to about 50%.
3. The process of claim 1 , wherein the surfactants are selected from the group consisting of poly(ethylene glycol)-400 dioleate, poly(ethylene glycol)-8 dioleate, sorbitan laurate, poly(ethylene glycol)-40 sorbitan peroleate, lecithin glycol distearate, sorbitan trioleate and propylene glycol isostearate.
4. The process of claim 1 , wherein the surfactants comprise one selected from the group consisting of poly(ethylene glycol)-8 dioleate, sorbitan laurate, poly(ethylene glycol)-40 sorbitan peroleate and lecithin, and another selected from the group consisting of glycol distearate, sorbitan trioleate and propylene glycol isostearate.
5. The process of claim 1 , wherein the surfactants comprise poly(ethylene glycol)-400 dioleate and sorbitan trioleate.
6. The process of claim 1 , wherein the polymeric shell comprises at least one selected from the group consisting of polyurethane, polyurea, poly(urea-urethane), polystyrene, and urea-formaldehyde polymer.
7. The process of claim 1 , wherein the microcapsule comprises a size of about 100 microns to about 200 microns, and the polymeric shell comprises a thickness of about 30 microns to about 50 microns.
8. The process of claim 1 , wherein the encapsulating step comprises a stirring step at a speed of about 700-950 rpm.
9. The process of claim 1 , further comprising adding surfactants.
10. The process of claim 1 , further comprising embedding a plurality of the microcapsules in a concrete mixture.