Composite biofabricated material
The invention is directed to a composite material comprising a biofabricated material and a secondary component. The secondary component may be a porous material, such as a sheet of paper, cellulose, or fabric that has been coated or otherwise contacted with the biofabricated material. The biofabricated material comprises a uniform network of crosslinked collagen fibrils and provides strength, elasticity and an aesthetic appearance to the composite material.
1. A composite material, comprising:
at least one secondary component; and
at least one collagen-based material, the collagen-based material comprising:
a network of recombinant non-human collagen fibrils;
5% to 25% water by weight of the collagen-based material; and
0.1% to 60% of a lubricant by weight of the collagen-based material,
wherein 1% to 40% by weight of the recombinant non-human collagen fibrils within the network of recombinant non-human collagen fibrils are assembled in the form of recombinant collagen fibers comprising a plurality of the recombinant non-human collagen fibrils, and
wherein each of the recombinant collagen fibers has a diameter in a range of 1 μm to 10 μm.
2. The composite material of claim 1 , wherein the at least one collagen-based material is substantially uniformly dispersed, encapsulated, or incorporated into the at least one secondary component.
3. The composite material of claim 1 , wherein the composite material has: (a) a top surface and a bottom surface, or (b) an inner surface and an outer surface.
4. The composite material of claim 3 , wherein the collagen-based material is incorporated on at least one of the top surface, the bottom surface, the inner surface or the outer surface.
5. The composite material of claim 4 , wherein the at least one secondary component comprises at least one of a fabric material, a nonwoven fibrous material, or a woven fibrous material, and wherein the fabric material, the nonwoven fibrous material, or the woven fibrous material comprises at least one of: cotton, wool, cashmere, angora, linen, bamboo, bast, hemp, soya, seacell, fibers produced from milk proteins, silk, spider silk, chitosan, mycelium, cellulose, wood fibers, nylon, polyester, a polyester-polyurethane copolymer, an aramid, carbon fibers, fullerenes, glass fibers, silicon, mineral particles, mineral fibers, a metal, or a metal alloy.
6. The composite material of claim 3 , wherein the collagen-based material is incorporated on both the top surface and the bottom surface, or both the inner surface and the outer surface.
7. The composite material of claim 1 , wherein the at least one secondary component comprises at least one of a resin, a polymer, or a plastic.
8. The composite material of claim 1 , wherein the at least one secondary component comprises at least one of a mesh, a woven material, or a nonwoven material, and wherein the mesh, the nonwoven fibrous material, or the woven fibrous material comprises at least one of: cotton, wool, cashmere, angora, linen, bamboo, bast, hemp, soya, seacell, fibers produced from milk proteins, silk, spider silk, chitosan, mycelium, cellulose, wood fibers, nylon, polyester, a polyester-polyurethane copolymer, an aramid, carbon fibers, fullerenes, glass fibers, silicon, mineral particles, mineral fibers, a metal, or a metal alloy.
9. The composite material of claim 1 , wherein the collagen-based material comprises 0.1% to 1% of at least one protein by weight of the collagen-based material, wherein the at least one protein is selected from the group consisting of actin, keratin, elastin, fibrin, albumin, globulin, mucin, mucinoids, noncollagen structural proteins, and noncollagen nonstructural proteins.
10. The composite material of claim 1 , wherein the collagen-based material is substantially free of non-collagenous proteins, carbohydrates, nucleic acids, lipids, immunogens, antigens, and allergens.
11. The composite material of claim 1 , wherein the collagen-based material comprises 1% to 10% of at least one crosslinking agent by weight of the collagen-based material.
12. The composite material of claim 1 , wherein the recombinant non-human collagen fibrils have a substantially unimodal distribution of diameters, further wherein 70% to 99% of the diameters are distributed around a single mode.
13. The composite material of claim 1 , wherein the lubricant is selected from the group consisting of fat, biological oil, mineral oil, synthetic oil, sulfonated oil, polymer, organofunctional siloxane, and combinations thereof.
14. The composite material of claim 1 , wherein the collagen-based material further comprises at least one photoluminescent agent.
15. The composite material of claim 1 , wherein the collagen-based material further comprises at least one of an electrically conductive agent or a magnetic agent.
16. The composite material of claim 1 , wherein the collagen-based material has a substantially uniform elastic modulus ranging from 100 kPa to 100 MPa, and a substantially uniform tensile strength ranging from 1 MPa to 100 MPa.
17. The composite material of claim 1 , wherein the collagen-based material further comprises at least one of a surface coating or a surface finish.
18. The composite material of claim 1 , wherein the collagen-based material further comprises at least one of a dye, a stain, a resin, a polymer, a pigment or a paint, wherein the dye, the stain, the resin, the pigment or the paint is distributed substantially uniformly throughout the collagen-based material.
19. The composite material of claim 1 , wherein the collagen-based material further comprises at least one filler, and wherein the at least one filler is distributed substantially uniformly throughout the material.
20. The composite material of claim 1 , wherein the recombinant non-human collagen fibrils comprise collagen having substantially no 3-hydroxyproline.
21. The composite material of claim 1 , wherein the recombinant non-human collagen fibrils comprise collagen having substantially no hydroxylysine.
22. The composite material of claim 1 , wherein 1% to 5% by weight of the recombinant non-human collagen fibrils are assembled in the form of the recombinant collagen fibers and have a diameter ranging from 1 μm to 5 μm.
23. The composite material of claim 1 , wherein 1% to 10% by weight of the recombinant non-human collagen fibrils are assembled in the form of the recombinant collagen fibers and have a diameter ranging from 5 μm to 10 μm.
24. The composite material of claim 1 , wherein the collagen-based material further comprises 0.1% to 1% actin by weight of the collagen-based material, and wherein the recombinant non-human collagen fibrils comprise recombinant non-human collagen isolated from cells that are cultured in vitro.
25. The composite material of claim 1 , wherein the recombinant non-human collagen fibrils comprise purified recombinant non-human collagen.
26. The composite material of claim 1 , wherein the collagen-based material comprises 25% to 99% by weight of recombinant non-human collagen based on a total protein content of the collagen-based material.
27. The composite material of claim 1 , wherein the secondary component comprises at least one of a porous material, a permeable material, or an absorptive material.
28. The composite material of claim 1 , wherein each of the recombinant non-human collagen fibrils has a diameter in a range of 1 nm to 1 μm.
29. The composite material of claim 1 , wherein the network of recombinant non-human collagen fibrils has a collagen fibril density in a range of 1 mg/cc to 1,000 gm/cc.