Encapsulant modification in heavily phosphor loaded LED packages for improved stability
View Patent ↗Heavily phosphor loaded LED packages having higher stability and a method for increasing the stability of heavily phosphor loaded LED packages. The silicone content of the packages is increased by decreasing the amount of one phosphor of the blend or by increasing the thickness of the silicone phosphor blend layer.
1. An LED package, comprising:
an LED positioned within an LED package cavity;
a phosphor silicone blend layer overlayed on the LED within the LED package cavity, wherein the LED is retained in the LED package cavity at least in part by the phosphor silicone blend layer, the phosphor silicone blend layer having a depth of 400 to 900 microns and the weight percent of silicone in the phosphor silicone blend layer is 54 to 75;
wherein a weight percent of total phosphor to silicone is 20% or higher, the total phosphor comprising K 2 [SiF 6 ]:Mn 4+ phosphor and a blue-shifted yellow (BSY) phosphor;
and wherein the phosphor silicone blend layer comprises K 2 [SiF 6 ]:Mn 4+ phosphor in an amount of 19-36 wt % and the blue-shifted yellow (BSY) phosphor in an amount of 4-9 wt %.
2. The LED package of claim 1 wherein the LED package cavity depth is from 450 to 900 microns.
3. The LED package of claim 1 , wherein the weight percent of silicone in the phosphor silicone blend is 58 to 75.
4. The LED package of claim 1 , wherein the LED is of power less than 1 W.
5. The LED package of claim 1 , wherein the phosphor silicone blend further comprises Yttrium Aluminum Garnet (YAG) phosphor.
6. The LED package of claim 1 , wherein a weight percent of total phosphor to silicone is 30% or higher.
7. A phosphor loaded LED package, comprising:
an LED positioned within an LED package cavity;
a phosphor silicone blend layer overlayed on the LED within the LED package cavity, wherein the LED is retained in the LED package cavity at least in part by the phosphor silicone blend layer, wherein the weight percent of silicone in the phosphor silicone blend layer is 54 to 75, wherein a weight percent of total phosphor to silicone is 20% or higher, and wherein the phosphor silicone blend layer comprises the total phosphor formed from a blue-shifted yellow (BSY phosphor and a narrow red phosphor comprising K 2 [SiF 6 ]:Mn 4+ , wherein the amount of K 2 [SiF 6 ]:Mn 4+ in the phosphor silicone blend layer is 19-36 wt %, and wherein the amount of BSY in the phosphor silicone blend layer is 4-9 wt %.
8. A phosphor loaded LED package of claim 7 wherein the phosphor silicone blend further comprises Yttrium Aluminum Garnet (YAG) phosphor.
9. An LED package containing a phosphor silicone blend and having improved color stability, the package comprising:
an LED and a phosphor silicone blend layer encapsulating the LED,
wherein the phosphor silicone blend layer comprises silicone, and YAG and K 2 [SiF 6 ]:Mn 4+ phosphors;
wherein the amount of K 2 [SiF 6 ]:Mn 4+ in the phosphor silicone blend layer is 35-40 wt %;
wherein the amount of YAG in the phosphor silicone blend layer is 10-12 wt %; and
wherein the amount of silicone in the phosphor silicone blend layer is 48-52 wt %.