Treatment of filaments or yarn
View Patent ↗A method for treating an aromatic polyamide filament or yarn to improve its adhesion to rubber wherein, the method comprises exposing the filament or yarn to a first mixture of reagents comprising multi-functional isocyanate oligomers and multi-functional epoxy oligomers, wherein the ratio of total isocyanate groups to total epoxy groups in the mixture is in the range of from 0.8 to 1.2, and heating the exposed filament or yarn to a temperature of at least 100 degrees C. whereby the epoxy and isocyanate oligomers cross-link and form a network on the surface of the filament or yarn.
1. A method for treating a filament or yarn comprising:
(a) forming a first mixture of reagents comprising first multi-functional isocyanate oligomers and first multi-functional epoxy oligomers, wherein the ratio of total isocyanate groups to total epoxy groups in the first mixture is in the range of from 0.8 to 1.2,
(b) dipping a filament or yarn into the first mixture of reagents,
(c) removing solvent from the dipped filament or yarn,
(d) dipping the filament or yarn from step (c) into a catalyst whereby the first isocyanate oligomers and the first epoxy oligomers form a network on the surface of the filament or yarn,
(e) forming a second mixture of reagents comprising second multi-functional isocyanate oligomers and second multi-functional epoxy oligomers, wherein the ratio of total isocyanate groups to total epoxy groups in the second mixture is in the range of from 0.8 to 1.2,
(f) dipping the filament or yarn of step (d) into the second mixture of reagents, and
(g) dipping the filament or yarn from step (f) into a catalyst whereby the second isocyanate oligomers and the second epoxy oligomers react to crosslink and form a network on the outer surface of the network formed by the first epoxy and first isocyanate oligomers of step (d), with the proviso that the double bonds present in the second epoxy and second isocyanate oligomers do not participate in the crosslinking reaction.
2. The method of claim 1 , wherein the first and second multi-functional isocyanate oligomers contain two or more isocyanate functional groups and the first and second multi-functional epoxy oligomers contain two or more epoxide rings.
3. The method of claim 1 wherein the filament or yarn is synthetic and is selected from the group consisting of an aromatic polyamide, an aromatic copolyamide, an aliphatic polyamide and polyester.
4. The method of claim 3 , wherein the aromatic polyamide is para-aramid.
5. The method of claim 1 wherein the filament or yarn is natural and is selected from the group consisting of cotton or cellulose.
6. The method of claim 1 wherein the filament or yarn is in a form selected from the group consisting of a cord and a fabric.
7. The method of claim 1 , wherein, the first and second multi-functional isocyanate oligomers of the first and second mixtures are different.
8. The method of claim 1 , wherein the first and second epoxy oligomers of the first and second mixtures are different.
9. A method for bonding a filament or yarn to un-cured rubber, the method comprising
(i) forming a treated filament or yarn by the method of claim 1 ,
(ii) heating the treated filament or yarn of step (i) in the presence of un-cured rubber whereby the networks of double bonds on the surface of the filament or yarn co-cure into the rubber matrix.