Adhesive compositions and methods for coating objects
An adhesive composition comprising a core shell vinyl ester and a urethane acrylate, which is suitable to be applied to a rough or uneven surface of a substrate to render a smooth surface. The present adhesive composition is particularly suitable to coat large objects made through additive manufacturing to form molds or prototypes.
1. A polymer composite article comprising:
a substrate comprising a polymer body having a surface with a surface profile in the range of 1.0 to 10 mm; and,
an adhesive coating on the surface of the polymer body, wherein the adhesive coating comprises core shell vinyl ester resin, wherein the adhesive coating has a surface profile of less than 0.10 mm after applying the adhesive coating.
2. The polymer composite article of claim 1 , wherein the adhesive coating further comprises a urethane acrylate and, optionally one or more additives.
3. The polymer composite article of claim 1 , wherein the adhesive coating, when cured, has an average thickness of greater than 0.08 inches.
4. The polymer composite article of claim 1 , wherein the substrate comprises acrylonitrile butadiene styrene, polyphenylene sulfide, polyphenylsulfone, polyethersulfone, polyethylene terephthalate, polybutylene terephthalate, polylactic acid, or combinations thereof, each of which may be optionally reinforced with glass fibers, carbon fibers, bamboo, or combinations thereof.
5. The polymer composite article of claim 1 , wherein bond strength between the surface of the substrate and the adhesive coating after the adhesive coating is cured is at least 300 psi.
6. A method of manufacturing a polymer composite article comprising:
(a) forming a substrate comprising a polymer body having a surface with a surface profile in the range of 1.0 to 10 mm;
(b) applying an adhesive coating on the surface of the polymer body, wherein the adhesive coating comprises core shell vinyl ester resin;
(c) curing the adhesive coating, wherein the adhesive coating has a surface profile of less than 0.10 mm after applying the adhesive coating.
7. The method of manufacturing a polymer composite article of claim 6 , wherein the adhesive coating further comprises a urethane acrylate and, optionally one or more additives.
8. The method of manufacturing a polymer composite article of claim 6 , wherein the substrate comprises acrylonitrile butadiene styrene, polyphenylene sulfide, polyphenylsulfone, polyethersulfone, polyethylene terephthalate, polybutylene terephthalate, polylactic acid, or combinations thereof, each of which may be optionally reinforced with glass fibers, carbon fibers, bamboo, or combinations thereof.
9. The method of manufacturing a polymer composite article of claim 6 , wherein the applying step comprises applying the adhesive coating to achieve a layer with a thickness of greater than 0.08 inches.
10. The method of manufacturing a polymer composite article of claim 6 , further comprising:
(d) cooling the cured adhesive coating to within 10° F. of the initial temperature of the surface of the substrate;
(e) applying an additional layer of the adhesive coating;
(f) curing the adhesive coating applied in step (e); and optionally,
(g) repeating steps (d)-(f) until the desired average thickness of the adhesive coating is achieved.
11. The method of manufacturing a polymer composite article of claim 6 , wherein the adhesive coating is applied by spraying the adhesive coating onto the surface of the polymer body, or by applying the composition with a squeegee, roller, trowel, spatula, paint stick, or paint brush.