Resin-compatible laminate structures

1. A laminate structure suitable for use as electrical insulation, comprising:

a) a first paper layer comprising 90 to 99 weight percent uniformly distributed calcined mica and 1 to 10 weight percent supporting material, a majority by weight of the supporting material being in the form of an aramid floc, the supporting material further comprising a binder that is an aramid fibrid; and

b) a support layer comprising unidirectional filaments or unidirectional yarns or woven yarns, the support layer having a first and second face;

wherein the first face of the support layer is directly bound to a face of the first paper layer;

the laminate structure having a dielectric strength of 15 kV/mm or greater, a Gurley porosity of 400 seconds or less, and a total mica content of 60 weight percent or greater,

wherein the floc in the first paper layer is present in an amount of 60 weight percent or greater, based on the total amount of the supporting material in the first paper layer.

2. The laminate structure of claim 1 wherein the floc in the first paper layer is present in an amount of 80 weight percent or greater, based on the total amount of the supporting material in the first paper layer.

3. The laminate structure of claim 1 wherein the aramid is poly(metaphenylene isophthalamide).

4. The laminate structure of claim 1 further including an adhesive on the first or second face of the support layer.

5. The laminate structure of claim 1 wherein the filaments or fibers of the support layer comprise glass filaments or fibers.

6. The laminate structure of claim 1 in the form of a tape having a width of 0.635 to 5.1 centimeters (0.25 to 2 inches).

7. The laminate structure of claim 1 further comprising an impregnating resin, varnish, or mixture thereof.

8. A laminate structure suitable for use as electrical insulation, comprising:

a) a first paper layer comprising 90 to 99 weight percent uniformly distributed calcined mica and 1 to 10 weight percent supporting material, a majority by weight of the supporting material being in the form of an aramid floc, the supporting material further comprising a binder that is an aramid fibrid;

b) a support layer comprising unidirectional or woven filament yarns, the support layer having a first and second face; and

c) a second paper layer comprising 90 to 99 weight percent uniformly distributed calcined mica and 1 to 10 weight percent supporting material, a majority by weight of the supporting material being in the form of an aramid floc, the supporting material further comprising a binder that is an aramid fibrid;

wherein the first face of the support layer is directly bound to a face of the first paper layer and the second face of the support layer is directly bound to a face of the second paper layer; and

the laminate structure having a total mica content of 60 weight percent or greater,

wherein the floc in both the first and the second paper layer is present in an amount of 60 weight percent or greater, based on the total amount of the supporting material in the respective paper layer.

9. The laminate structure of claim 8 having a dielectric strength of 15 kV/mm or greater and a Gurley porosity of 400 seconds or less.

10. The laminate structure of claim 9 wherein the floc in both the first and the second paper layer is present in an amount of 80 weight percent or greater, based on the total amount of the supporting material in the respective paper layer.

11. The laminate structure of claim 8 further including an adhesive on the first or second face of the support layer.

12. The laminate structure of claim 8 wherein the filaments or fibers of the support layer comprise glass filaments or fibers.

13. The laminate structure of claim 8 in the form of a tape having a width of 0.635 to 5.1 centimeters (0.25 to 2 inches).

14. The laminate structure of claim 8 further comprising an impregnating resin, varnish, or mixture thereof.