Multi-layered aluminium brazing sheet material
View Patent ↗Multilayered brazing sheet including aluminium core alloy layer of 3xxx-series aluminium alloy having, in wt. %, up to 0.4% Si, up to 0.5% Fe, 0.4% to 0.75% Cu, 0.6% to 1.1% Mn, up to 0.07% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.2% Ti, up to 0.15% Zn, balance aluminium and impurities, first and second brazing clad layers on opposed faces of core layer, and an inter-layer on either or both sides of core layer between the core layer and first or second brazing clad layer. The first and second brazing layers are 4xxx-series aluminium alloy. The inter-layer(s) is 3xxx-series aluminium alloy, having, in wt. %, up to 0.6% Si, 0.2% to 0.7% Fe, up to 0.2% Cu, 1.0% to 1.6% Mn, up to 0.25% Zn, up to 0.04% Mg, up to 0.2% Cr, up to 0.2% Zr, up to 0.07% Ti, balance aluminium and impurities.
1. A multi-layered brazing sheet material consisting of an aluminium core alloy layer provided with a first brazing clad layer material on one face of said aluminium core alloy layer and a second brazing clad layer material on another face of said aluminium core alloy layer, and an inter-layer on one or either sides of the aluminium core alloy layer positioned between the aluminium core alloy layer and the first brazing clad layer material or the second brazing clad layer material,
wherein the aluminium core alloy layer is made from a 3xxx-series aluminium alloy having, in wt. %, up to 0.4% Si, up to 0.5% Fe, 0.4% to 0.75% Cu, 0.6% to 1.1% Mn, up to 0.07% Mg, up to 0.2% Cr, up to 0.25% Zr, up to 0.2% Ti, and up to 0.15% Zn, balance aluminium and impurities,
wherein the first brazing clad layer material and the second brazing clad layer material are made from a 4xxx-series aluminium alloy having 6% to 14% Si, up to 2% Mg, and up to 0.2% Zn, balance aluminium and impurities, and
wherein the inter-layer(s) is made from an aluminium alloy of the 3xxx-series alloys, having, in wt. %, up to 0.6% Si, 0.2% to 0.7% Fe, up to 0.2% Cu, 1.0% to 1.6% Mn, up to 0.1% Zn, up to 0.04% Mg, up to 0.2% Cr, up to 0.2% Zr, and up to 0.07% Ti, balance aluminium and impurities,
wherein the aluminium core alloy layer has been homogenised.
2. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer is made from an aluminium alloy consisting of, in wt. %, up to 0.2% Si, 0.15% to 0.45% Fe, 0.50% to 1.0% Mn, up to 0.02% Mg, up to 0.09% Cr, up to 0.09% Zr, 0.05% to 0.2% Ti, and up to 0.15% Zn, balance aluminium and impurities.
3. The brazing sheet material according to claim 1 , wherein the aluminium core alloy layer is made from an aluminium alloy consisting of, in wt. %, up to 0.2% Si, 0.25% to 0.45% Fe, 0.50% to 0.68% Cu, 0.7% to 0.95% Mn, up to 0.02% Mg, up to 0.04% Cr, up to 0.04% Zr, 0.06% to 0.12% Ti, and up to 0.15% Zn, balance aluminium and impurities.
4. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material is made from a 4xxx-series aluminium alloy having 6% to 14% Si and up to 0.35% Mg, balance impurities and aluminium.
5. The brazing sheet material according to claim 1 , wherein the inter-layer(s) is made from a 3xxx-series alloy consisting of, in wt. %, 0.15% to 0.55% Si, 0.2% to 0.65% Fe, up to 0.15% Cu, 1.0% to 1.5% Mn, up to 0.1% Zn, up to 0.04% Mg, up to 0.2% Cr, up to 0.2% Zr, and up to 0.06% Ti, balance aluminium and impurities.
6. The brazing sheet material according to claim 1 , wherein the inter-layer(s) is made from a 3xxx-series alloy consisting of, in wt. %, 0.2% to 0.5% Si, 0.25% to 0.65% Fe, up to 0.15% Cu, 1.1% to 1.4% Mn, up to 0.1% Zn, up to 0.04% Mg, up to 0.2% Cr, up to 0.2% Zr, and 0.02% to 0.06% Ti, balance aluminium and impurities.
7. The brazing sheet material according to claim 1 , and wherein each inter-layer has a thickness of 90 μm.
8. The brazing sheet material according to claim 1 , wherein the multi-layered brazing sheet material has a total thickness of 0.1 to 2.0 mm.
9. The brazing sheet material according to claim 1 , wherein the brazing sheet material is provided in an O-temper.
10. A brazing tube made from the multi-layered brazing sheet material according to claim 1 .
11. A heat exchanger comprising a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
12. A charge-air-cooler incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
13. The multi-layered brazing sheet material according to claim 1 as a brazed tube in a charge-air-cooler.
14. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material and second brazing clad layer material are each made from a 4xxx-series aluminium alloy having 6% to 14% Si and up to 0.10% Mg, balance impurities and aluminium.
15. The brazing sheet material according to claim 1 , wherein each inter-layer has a thickness of 60 μm or less.
16. An air-to-water charge-air-cooler incorporating a brazed tube made from the multi-layered brazing sheet material according to claim 1 .
17. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material and the second brazing clad layer material are each made from a 4xxx-series aluminium alloy having 6% to 14% Si and up to 0.35% Mg, balance impurities and aluminium.
18. The brazing sheet material according to claim 1 , wherein the first brazing clad layer material and the second brazing clad layer material are made from the 4xxx-series aluminium alloy consisting of 6% to 14% Si, and up to 2% Mg, balance aluminium and impurities.
19. The brazing sheet material according to claim 1 , wherein the inter-layer(s) consists of the aluminium alloy of the 3xxx-series alloys, having, in wt. %, up to 0.6% Si, 0.2% to 0.7% Fe, up to 0.2% Cu, 1.0% to 1.6% Mn, up to 0.04% Mg, up to 0.2% Cr, up to 0.2% Zr, and up to 0.07% Ti, balance aluminium and impurities.