Multilayer structure comprising polypropylene

1. A multilayer structure comprising, or produced from, a polyolefin layer, an adhesive layer, a barrier layer, and, optionally, an additional layer, wherein:

the adhesive layer comprises or is produced from a composition comprising (1) a first ethylene α-olefin copolymer, (2) a modified first ethylene α-olefin copolymer, and (3) a second ethylene α-olefin copolymer or a propylene α-olefin copolymer;

the total weight of the first ethylene α-olefin copolymer and the modified first ethylene α-olefin copolymer is from about 65 to about 85%, based on the total weight of the composition;

the modified first ethylene α-olefin copolymer is a base ethylene α-olefin copolymer that has been grafted with a dicarboxylic acid, an anhydride of the dicarboxylic acid, or combinations thereof;

the first ethylene α-olefin copolymer contains ≤5 mole % of α-olefin, has a DSC melting point ≥115° C., and has an enthalpy of fusion, as measured by DSC in the second heat, ≥100 J/g; and

the second ethylene α-olefin copolymer or propylene α-olefin copolymer can be present in the composition from about 15 wt % to about 35 wt %, based on the total weight of the composition.

2. The multilayer structure of claim 1 wherein

the adhesive layer is in direct contact with the polyolefin layer and the barrier layer; and

the modified first ethylene α-olefin copolymer contains 0.03 to 3 weight %, based on the graft concentration in the composition, of a dicarboxylic acid moiety or an anhydride moiety of the dicarboxylic acid.

3. The multilayer structure of claim 1 wherein the base ethylene α-olefin copolymer is different from the first ethylene α-olefin copolymer.

4. The multilayer structure of claim 1 wherein

the second ethylene α-olefin copolymer contains ≥8 mole % of a C 4 to C 8 even numbered α-olefin, has a DSC melting point of 115° C. or higher, and has an enthalpy of fusion, as measured by DSC in the second heat, of 80 j/g or lower; or

the propylene α-olefin copolymer contains ≥8 mole % of one or more C 2 to C 8 even-numbered α-olefin and has an enthalpy of fusion, as measured by DSC in the second heat, of 80 J/g or lower.

5. The multilayer structure of claim 2 further comprising a tie layer disposed on a side of the barrier layer opposite to the adhesive layer, wherein the tie layer is the same as, or different from, the adhesive layer.

6. The multilayer structure of claim 5 wherein the tie layer is the same as the adhesive layer.

7. The multilayer structure of claim 5 further comprising a second polyolefin layer in contact with the tie layer and opposite to the barrier layer.

8. The multilayer structure of claim 1 wherein the barrier layer comprises a plurality of barrier layers selected from the group consisting of one or more polyamide layers, one or more EVOH layers, and combinations thereof.

9. The multilayer structure of claim 1 having one or more of the following structures

PP/tie/barrier layer(s)/tie/PE

PA/tie/PP/tie/barrier layer(s)/tie/PE/PE/EVA or ionomer

HomoPP/coPP/tie/PE/tie/barrier(s)/tie/PE/PE/mPE

HomoPP/coPP/tie/PA/EVOH/PA/tie/LLDPE/VLDPE;

HomoPP/coPP/tie/PE/tie/PA/EVOH/PA/tie/PE/PE/PE/mPE;

PA/tie/coPP/tie/PA/tie/EVA/EVA;

PA/tie/coPP/coPP/tie/PA/EVOH/PA/tie/ethylene acid copolymer/ethylene ionomer;

coPP/tie/EVOH/tie/mPE;

HomoPP/coPP/tie/PA/EVOH/PA/tie/ethylene ionomer/ethylene acid copolymer; and

PET/EMA/coPP/tie/PA/EVOH/PA/tie/ethylene ionomer/ethylene ionomer;

wherein the “/” denotes between layers, “Homo” means homopolymer, “PP” is polypropylene layer, “coPP” denotes layer of copolymer of propylene and α-olefin, “PA” is a polyamide layer, “EVOH” is ethylene vinyl alcohol layer, “LLDPE” is a linear low density polyethylene layer, “VLDPE” is a very low density polyethylene layer, “tie” is a tie layer and wherein at least one tie layer is the adhesive layer, “EVA” is an ethylene vinyl acetate copolymer layer, “mPE” is a layer of polyethylene produced by metallocene catalysis, “PET” is a polyethylene terephthalate layer, and “EMA is an ethylene methacrylate copolymer layer.

10. A process of manufacturing the multilayer structure of claim 1 , the process comprising coextruding the polyolefin layer, the adhesive layer, the barrier layer, and optionally, the additional layer under a condition effective to produce a blown film; quenching the blown film in less than about 12 seconds to produce a quenched film; collapsing the quenched film to a flat tubular film; optionally, slitting the flat tubular film to produce a slit flat film; and collecting the slit flat film or the flat tubular film to produce the multilayer structure wherein

the adhesive layer is in direct contact with the polyolefin layer and the barrier layer.

11. A process of manufacturing the multilayer structure of claim 1 , the process comprising coextruding the polyolefin layer, the adhesive layer, the barrier layer, and optionally, the additional layer through a flat die to produce a cast film; quenching the cast film on a chilled casting roll to produce a quenched film optionally, slitting the quenched film to produce a slit film; and collecting the quenched film or the slit film to produce the multilayer structure, wherein:

the adhesive layer is in direct contact with the polyolefin layer and the barrier layer.

12. A process of manufacturing the multilayer structure of claim 1 , the process comprising coextruding the polyolefin layer, the adhesive layer, the barrier layer, and optionally, the additional layer under a condition effective to produce a coextruded tubular multilayer structure; cooling the coextruded tubular multilayer structure in a first bubble; orienting the coextruded tubular multilayer structure under heating in a second bubble to produce an oriented tubular multilayer structure; and relaxing the oriented tubular multilayer structure under heating in a third bubble to produce the multilayer structure wherein

the adhesive layer is in direct contact with the polyolefin layer and the barrier layer.

13. A process of manufacturing the multilayer structure of claim 1 , the process comprising coextruding the polyolefin layer, the adhesive layer, the barrier layer, and optionally, the additional layer through a flat die to produce a cast film or sheet; quenching the cast film or sheet on a chilled casting roll to produce a quenched film or sheet; heating the quenched film or sheet from about 60° C. to about 100° C. to produce a heated film or sheet; stretching the heated film or sheet to produce an oriented film or sheet; optionally, slitting the oriented film or sheet to produce a slit film; and collecting the oriented film or sheet or the slit film or sheet to produce the multilayer structure, wherein

the adhesive layer is in direct contact with the polyolefin layer and the barrier layer.

14. A composition comprising or produced from (1) a first ethylene α-olefin copolymer, (2) a modified first ethylene α-olefin copolymer, and (3) a second ethylene α-olefin copolymer or a propylene α-olefin copolymer; wherein:

the total weight of the first ethylene α-olefin copolymer and the modified first ethylene α-olefin copolymer is from about 65 to about 85%, based on the total weight of the composition;

the modified first ethylene α-olefin copolymer is a base ethylene α-olefin copolymer that has been grafted with a dicarboxylic acid, an anhydride of the dicarboxylic acid, or combinations thereof;

the first ethylene α-olefin copolymer contains ≤5 mole % of α-olefin, has a DSC melting point ≥115° C., and has an enthalpy of fusion, as measured by DSC in the second heat, ≥100 J/g; and

the second ethylene α-olefin copolymer or propylene α-olefin copolymer can be present in the composition from about 15 wt % to about 35 wt %, based on the total weight of the composition.

15. The composition of claim 14 , wherein the base ethylene α-olefin copolymer is different from the first ethylene α-olefin copolymer.

16. The composition of claim 14 , wherein:

the second ethylene α-olefin copolymer contains ≥8 mole % of a C 4 to C 8 even numbered α-olefin, has a DSC melting point of 115° C. or higher, and has an enthalpy of fusion, as measured by DSC in the second heat, of 80 J/g or lower; or

the propylene α-olefin copolymer contains ≥8 mole % of one or more C 2 to C 8 even-numbered α-olefin and has an enthalpy of fusion, as measured by DSC in the second heat, of 80 J/g or lower.