Electrode material, and electrode layer, battery, and electrochromic device using the electrode material
The present invention provides an electrode material comprising at least one of metal compound powder and carbon powder, the powder having an average particle size of 50 μm or less and an activation energy E α of 0.05 eV or less. Further, the powder preferably has hopping conduction characteristics at room temperature of 25° C. Furthermore, the powder preferably has an amount of oxygen defects of 1×10 18 cm −3 or more. Still further, the powder preferably has a carrier density of 1×10 18 cm −3 or more. Due to above structure, there can be provided an electrode material having a high storage capacity and a high charge/discharge efficiency.
1. An electrode material comprising at least one metal compound powder selected from the group consisting of tungsten oxide, molybdenum oxide, Mo x W y O z , where 0<x≤1, 0<y≤1, x+y=1, and 2≤z≤3, lithium tungstate, lithium molybdate and molybdenum sulfide,
wherein the at least one metal compound powder has an average particle size of 50 μm or less, an activation energy E α of 0.05 eV or less, a carrier density of 1×10 18 cm −3 or more, and wherein an amount of oxygen defects in the at least one metal compound powder is 1×10 18 cm −3 or more.
2. The electrode material according to claim 1 , wherein the at least one metal compound powder has hopping conduction characteristics at room temperature of 25° C.
3. The electrode material according to claim 1 , wherein the at least one metal compound powder has hopping conduction characteristics with a 1000/T value in a range of 2.8 to 4.0 when a measurement temperature is referred to as T (° K).
4. The electrode material according to claim 1 , wherein the at least one metal compound powder has a resistivity of 10 Ωcm or less at room temperature of 25° C.
5. The electrode material according to claim 1 , wherein the at least one metal compound powder has an average particle size of 10 μm or less.
6. An electrode layer comprising 50 mass % or more and 100 mass % or less of the electrode material according to claim 1 .
7. A battery comprising the electrode layer according to claim 6 .
8. The battery according to claim 7 , comprising the electrode layer as an anode.
9. An electrochromic device comprising the electrode material according to claim 1 .
10. The electrode material according to claim 1 , wherein the at least one metal compound powder has hopping conduction characteristics with a 1000/T value in a range of 2.8 to 4.0 when a measurement temperature is referred to as T (° K), and wherein the at least one metal compound powder has a resistivity of 10 Ωcm or less at room temperature of 25° C.
11. The battery according to claim 8 , wherein the at least one metal compound powder of the electrode material has hopping conduction characteristics with a 1000/T value in a range of 2.8 to 4.0 when a measurement temperature is referred to as T (° K).
12. The electrochromic device according to claim 9 , wherein the at least one metal compound powder of the electrode material has hopping conduction characteristics with a 1000/T value in a range of 2.8 to 4.0 when a measurement temperature is referred to as T (° K).