Mold flux for continuous-casting steel
Provided is mold flux that can prevent longitudinal cracks from forming on a surface of a slab upon continuous-casting hypo-peritectic steel, wherein CaO, SiO 2 , an alkali metal oxide and a fluorine compound are contained, 1.1≤(CaO) h /(SiO 2 ) h ≤1.9, 0.10≤(CaF 2 ) h /((CaO) h +(SiO 2 ) h +(CaF 2 ) h )≤0.40 and 0≤(alkali metal fluoride) h /((CaO) h +(SiO 2 ) h +(alkali metal fluoride) h )≤0.10 are satisfied, a solidification temperature is no less than 1300° C., and viscosity at 1450° C. is no more than 0.1 Pa·s.
1. Mold flux used for continuous-casting hypo-peritectic steel whose C concentration is 0.08 to 0.18 mass %, wherein
CaO, SiO 2 , an alkali metal oxide and a fluorine compound are contained,
the following formulas (1), (2) and (3) are satisfied, and
a solidification temperature is no less than 1300° C. and viscosity at 1450° C. is no more than 0.1 Pa·s:
1.1≤ f (1)≤1.9 (1)
0.10≤ f (2)≤0.40 (2)
0≤ f (3)≤0.10 (3)
wherein f (1)=(CaO) h /(SiO 2 ) h (a)
f (2)=(CaF 2 ) h /((CaO) h +(SiO 2 ) h +(CaF 2 ) h ) (b)
f (3)=(alkali metal fluoride) h /((CaO) h +(SiO 2 ) h +(alkali metal fluoride) h ) (c)
(CaO)h=(W CaO −(CaF 2 ) h ×0.718) (A)
(SiO 2 ) h =W SiO2 (B)
(CaF 2 ) h =(W F −W Li2O ×1.27−W Na2O ×0.613−W K2O ×0.403)×2.05 (C)
(alkali metal fluoride) h =W Li2O ×1.74+W Na2O ×1.35+W K2O ×1.23 (D)
wherein W i is a mass concentration of a component i in the mold flux and (CaO) h , (SiO 2 ) h , (CaF 2 ) h , and (alkali metal fluoride) h represent values based on results from calculations from the right side of equations (A), (C), and (D), and the right side of equality (B).
2. The mold flux for continuous-casting hypo-peritectic steel according to claim 1 , wherein the mold flux further contains 0.1-10 mass % of MnO.