Particle compositions for three-dimensional printing
Provided in one example herein is a three-dimensional printing method, comprising: (A) forming a layer comprising particles comprising a polymer and cavities between the particles, wherein the particles have an average diameter of between about 5 μm and about 250 μm; (B) disposing a liquid suspension over at least a portion of the layer such that the liquid suspension infiltrates into the cavities, wherein the liquid suspension comprises a radiation-absorbing coalescent agent and nanoparticles having an average diameter of less than or equal to about 500 nm; (C) forming an object slice by exposing the infiltrated layer to a radiant energy, wherein the object slice comprises a polymeric matrix comprising the polymeric particles, at least some of which are fused to one another, and the nanoparticles within the polymeric matrix; and (D) repeating (A) to (C) to form the three-dimensional object comprising multiple object slices bound depth-wise to one another.
1. A three-dimensional (“3D”) printing method, comprising:
(A) forming a layer comprising (i) mono-dispersed particles comprising a first polymer and (ii) cavities between the particles, wherein the particles have an average diameter of between about 5 μm and about 250 μm;
(B) disposing a liquid suspension over at least a portion of the layer such that the liquid suspension infiltrates into the cavities, wherein the liquid suspension comprises a radiation-absorbing coalescent agent and nanoparticles having an average diameter of less than or equal to about 300 nm, wherein the nanoparticles comprise a second polymer selected from the group consisting of a polyamide, a polystyrene, a polyethylene, a polyacetal, a polypropylene, a polycarbonate, and a polyurethane;
(C) forming an object slice of a 3D object by exposing the infiltrated layer to a radiant energy, wherein the object slice comprises a polymeric matrix comprising the particles, at least some of which are fused to one another, and the nanoparticles within the polymeric matrix; and
(D) repeating (A) to (C) to form the 3D object comprising multiple object slices bound depth-wise to one another.
2. The 3D printing method of claim 1 , wherein the first polymer comprises a polyamide having a weight-average molecular weight ranging from about 70,000 to about 300,000.
3. The 3D printing method of claim 1 , wherein the first polymer comprises at least one of thermoplastic polyurethane, PA-11, PA-12, PA-6, PA-8, PA-9, PA-66, PA-612, PA-812, and PA-912.
4. The 3D printing method of claim 1 , wherein the first polymer comprises at least one of a polyamide, a polystyrene, a polyethylene, a polyacetal, a polypropylene, a polycarbonate, and a polyurethane.
5. The 3D printing method of claim 1 , further comprising removing from the object slice particles that are not fused by at least one of brushing, water-jet cleaning, sonic cleaning, and blasting.
6. The 3D printing method of claim 1 , further comprising heating the layer to a temperature between about 5° C. below and about 50° C. below a melting temperature of the first polymer before (B).
7. A three-dimensional (“3D”) printing method, comprising:
(A) forming a layer comprising (i) mono-dispersed particles comprising a first thermoplastic and (ii) cavities between the particles, wherein the particles have an average diameter of between about 10 μm and about 150 μm;
(B) disposing an aqueous liquid suspension over at least a portion the layer such that the liquid suspension infiltrates into the cavities, wherein the liquid suspension comprises a radiation-absorbing coalescent agent and nanoparticles having an average diameter of between about 50 nm and about 500 nm, wherein the nanoparticles comprise a second thermoplastic;
(C) exposing the infiltrated layer to a radiant energy, such that the coalescent agent absorbs the energy and fuses at least some of the particles in the infiltrated layer;
(D) solidifying the exposed layer to form an object slice of a 3D object, wherein the object slice comprises a polymeric matrix comprising the fused particles and the nanoparticles within the polymeric matrix, and wherein the object slice is at least substantially free of the cavities; and
(E) repeating (A) to (C) to form the 3D object comprising multiple object slices bound depth-wise to one another.
8. The 3D printing method of claim 7 , further comprising fusing to one another at least one of (i) the particles, (ii) the nanoparticles, and (iii) a combination of (i) and (ii).
9. The 3D printing method of claim 7 , wherein the first thermoplastic is the same as the second thermoplastic.
10. The 3D printing method of claim 7 , further comprising disposing a modifier agent to at least one of (i) the object slice and (ii) the three-dimensional object to mitigate thermal bleed.
11. A three-dimensional (“3D”) printing system, comprising:
a supply of mono-dispersed particles comprising a first polymer and (ii) cavities between the particles, wherein the particles have an average diameter of between about 5 μm and about 250 μm;
a first device to form a layer of the mono-dispersed particles;
a supply of a liquid suspension comprising a radiation-absorbing coalescent agent and nanoparticles having an average diameter of less than or equal to about 300 nm, wherein the nanoparticles comprise a second polymer selected from the group consisting of a polyamide, a polystyrene, a polyethylene, a polyacetal, a polypropylene, a polycarbonate, and a polyurethane;
a second device to dispose the liquid suspension;
an energy source to apply a radiant energy; and
a controller to execute instructions to:
cause the first device to form the layer;
cause the second device to dispose over at least a portion of the layer the liquid suspension such that the liquid suspension infiltrates into the cavities; and
cause the energy source to apply the radiant energy to the infiltrated layer to form an object slice of a 3D object, wherein the object slice comprises a polymeric matrix comprising the particles, some of which are fused to one another, and the nanoparticles within the polymeric matrix.
12. The 3D printing system of claim 11 , wherein the second device comprises at least one of a thermal inkjet printer and a piezoelectric inkjet printer.
13. The 3D printing method of claim 7 , wherein each of the first and second thermoplastics comprises at least one of thermoplastic polyurethane, PA-11, PA-12, PA-6, PA-8, PA-9, PA-66, PA-612, PA-812, and PA-912.
14. A three-dimensional (“3D”) printing method, comprising:
(A) forming a layer comprising (i) mono-dispersed particles comprising a polymer and (ii) cavities between the particles, wherein the particles have an average diameter of between about 5 μm and about 250 μm;
(B) disposing a liquid suspension over at least a portion of the layer such that the liquid suspension infiltrates into the cavities, wherein the liquid suspension comprises a radiation-absorbing coalescent agent and nanoparticles having an average diameter of less than or equal to about 300 nm, wherein the nanoparticles comprise the same material as the particles;
(C) forming an object slice of a 3D object by exposing the infiltrated layer to a radiant energy, wherein the object slice comprises a polymeric matrix comprising the polymeric particles, at least some of which are fused to one another, and the nanoparticles within the polymeric matrix; and
(D) repeating (A) to (C) to form the 3D object comprising multiple object slices bound depth-wise to one another.
15. The 3D printing method of claim 10 , wherein the modifier agent includes an inorganic salt, a surfactant, a co-solvent, a humectant, a biocide, and water.