Dielectric composition, dielectric element, electronic component and laminated electronic component

1. A laminated electronic component comprising:

a laminated portion including alternating layers of internal electrode layers and dielectric layers, wherein the dielectric layers comprise a dielectric composition, the dielectric composition comprising:

a main component represented by (Bi a Na b Sr c Ln d )TiO 3 ,

wherein Ln is at least one element selected from the group consisting of: La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho and Yb, and

wherein a, b, c and d satisfy the following: 0<a<0.50, 0<b<0.50, 0<c≤0.80, 0<d≤0.20, and 0.90≤a+b+c+d≤1.05.

2. A dielectric composition comprising:

a main component represented by (Bi a Na b Sr c Ln d )TiO 3 ,

wherein Ln is at least one element selected from the group consisting of: Ce, Pr, Eu, Gd, Tb, Dy, Ho and Yb, and

wherein a, b, c and d satisfy the following: 0<a<0.50, 0<b<0.50, 0<c≤0.80, 0<d≤0.20, and 0.90≤a+b+c+d≤1.05.

3. The laminated electronic component as claimed in claim 1 , wherein a, b, c and d satisfy the following: 0.05<a≤0.40, 0.05<b≤0.40, 0<c≤0.70, 0<d≤0.04, and 0.90≤a+b+c+d≤1.05.

4. The laminated electronic component as claimed in claim 1 , wherein a=b.

5. The laminated electronic component as claimed in claim 1 , wherein Ln is at least one of La, Gd, or Yb.

6. The laminated electronic component as claimed in claim 1 , wherein a, b, c and d satisfy the following: 0.05<a≤0.40, 0.05<b≤0.40, 0<c≤0.70, 0<d≤0.10, and 0.90≤a+b+c+d≤1.05.

7. A method for forming a laminated electronic component, the method comprising:

providing a dielectric composition for dielectric layers by:

providing starting material powders of bismuth oxide (Bi 2 O 3 ) and sodium carbonate (Na 2 CO 3 ), strontium carbonate (SrCO 3 ) titanium oxide (TiO 2 ) and at least one of lanthanum hydroxide (La(OH) 3 ), cerium oxide (Ce 2 O 3 ), neodymium oxide (Nd 2 O 3 ), samarium oxide (Sm 2 O 3 ), gadolinium oxide (Gd 2 O 3 ), dysprosium oxide (Dy 2 O 3 ), or ytterbium oxide (Yb 2 O 3 ), wherein the starting material powders are weighed out in such a way that a dielectric composition after being sintered has a main component represented by (Bi a Na b Sr c Ln d )TiO 3 and the combination of a, b, c and d satisfy the following conditions: 0<a<0.50, 0<b<0.50, 0<c≤0.80, 0<d≤0.20, and 0.90≤a+b+c+d ≤1.05;

wet-mixing the weighed starting material powders;

obtaining a calcined article by calcining the mixture obtained by wet-mixing;

after drying the calcined article, wet-grounding the calcined article to obtain calcined powder; and

adding a binder to the calcined powder; and

stacking the dielectric layers and electrode layers thereby forming the laminated electronic component, wherein the dielectric layers comprise the dielectric composition.

8. The laminated electronic component according to claim 1 , wherein the laminated electronic component is a laminated ceramic capacitor comprising a capacitor element main body;

wherein the capacitor element main body comprises the laminated portion; and

wherein the laminated portion has the dielectric layers alternately stacked with the internal electrode layers.

9. The laminated electronic component according to claim 8 , further comprising a pair of terminal electrodes, wherein a terminal electrode of the pair of terminal electrodes is formed at each end of the capacitor element main body and wherein each terminal electrode of the pair of terminal electrodes conducts, respectively, with the internal electrode layers alternately arranged inside the element main body.

10. The laminated electronic component according to claim 9 , wherein each terminal electrode of the pair of terminal electrodes comprises a conductive material having silver (Ag), gold (Au), or copper (Cu) as the main component thereof.

11. The laminated electronic component according to claim 8 , wherein each internal electrode layer is substantially formed from a metal, wherein the metal is one of gold (Au), platinum (Pt), or silver (Ag).

12. The dielectric composition according to claim 2 , wherein the dielectric composition forms a disk-shaped dielectric body of a single-layer ceramic capacitor that comprises the disk-shaped dielectric body and a pair of electrodes.

13. The dielectric composition according to claim 12 , wherein the pair of electrodes of the single-layer ceramic capacitor having the disk-shaped dielectric body formed by the dielectric composition is substantially formed from at least one of silver (Ag), gold (Au), copper (Cu), platinum (Pt), or nickel (Ni).