Process for producing multimodal polyethylene blends including ultra-high molecular weight components
The present application relates to a process for producing a multimodal polyethylene composition comprising the steps of at least partially melting a first polyethylene resin (A) having a viscosity average molecular weight My of equal to or more than 700 kg/mol to equal to or less than 10,000 kg/mol and a density of equal to or more than 920 kg/m 3 to equal to or less than 960 kg/m 3 in a first homogenizing device, at least partially melting a second polyethylene resin (B) having a Mw of equal to or more than 50 kg/mol to less than 700 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 960 kg/m 3 in a second homogenizing device, combining the at least partially molten first polyethylene resin (A) with the at least partially molten second polyethylene resin (B) in said second homogenizing device, compounding the combined first polyethylene resin (A) and second polyethylene resin (B) in said second homogenizing device to form a multimodal polyethylene composition, wherein the multimodal polyethylene composition has a melt flow rate MFR 5 (190° C., 5 kg) of 0.01 to 10.0 g/10 min and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 and a polyethylene composition obtainable by said process.
1. A process for producing a multimodal polyethylene composition comprising the following steps:
i) at least partially melting a first polyethylene resin (A) having a viscosity average molecular weight My of equal to or more than 700 kg/mol to equal to or less than 10,000 kg/mol and a density of equal to or more than 920 kg/m 3 to equal to or less than 960 kg/m 3 in a first homogenizing device so that at least 20 wt % of the first polyethylene resin (A) is melted when exiting the first homogenization device,
ii) at least partially melting a second polyethylene resin (B) having a Mw of equal to or more than 50 kg/mol to 500 kg/mol, and a density of equal to or more than 910 kg/m 3 to equal to or less than 960 kg/m 3 in a second homogenizing device with at least a first feeding zone and a second feeding zone, the second feeding zone situated downstream of the first feeding zone, so that the second polyethylene resin (B) introduced into the first feeding zone is at least partially melted before reaching the second feeding zone of the second homogenizing device,
iii) combining the at least partially molten first polyethylene resin (A) with the at least partially molten second polyethylene resin (B) in said second homogenizing device,
iv) compounding the combined first polyethylene resin (A) and second polyethylene resin (B) in said second homogenizing device to form a multimodal polyethylene composition,
wherein the multimodal polyethylene composition has a melt flow rate MFR 5 (190° C., 5 kg) of 0.01 to 10.0 g/10 min and a density of equal to or more than 910 kg/m 3 to equal to or less than 970 kg/m 3 ;
wherein prior to the melting step i) the first polyethylene resin (A) is blended with a third polyethylene resin (C) and the blend of the first polyethylene resin (A) and the third polyethylene resin (C) is fed to the first homogenization device; and
wherein the second polyethylene resin (B) and the third polyethylene resin (C) are bimodal.
2. The process according to claim 1 , wherein the weight ratio of the first polyethylene resin (A) to the third polyethylene resin (C) in the blend of polyethylene resins (A) and (C) is from 45:55 to 80:20.
3. The process according to claim 1 , wherein the first polyethylene resin (A) is completely molten before combining with the second polyethylene resin (B).
4. The process according to claim 1 , said second homogenizing device is the main extruder for compounding the multimodal polyethylene composition.
5. The process according claim 4 , wherein said first homogenizing device is a side feed extruder having an exit which is connected to downstream of the melting zone of the main extruder.
6. The process according to claim 1 , wherein the weight ratio of the first polyethylene resin (A) to the second polyethylene resin (B) in the polyethylene composition is 0.5:99.5 to 50:50.
7. The process according to claim 2 , wherein the first polyethylene resin (A) is completely molten before combining with the second polyethylene resin (B).
8. The process according to claim 1 , wherein the process is performed adiabatically.