Adhesive composition for touch panels, adhesive film, and touch panel
Provided is an adhesive composition for touch panels, including: an acrylic resin; a first curing agent having one to three functional groups; and a second curing agent having four to six functional groups. Provided is an adhesive film including an adhesive layer, which is a cured product of the adhesive composition for touch panels. Provided is a touch panel including: a conductive plastic film which has a conductive layer formed on one side thereof; and an adhesive layer which is attached to the conductive layer and includes a cured product of the adhesive composition for touch panels.
1. An adhesive composition for touch panels, comprising:
an acrylic resin;
a first curing agent, which is a hexamethylene diisocyanate (HDI) derivative having two or three isocyanate groups; and
a second curing agent, which is a hexamethylene diisocyanate (HDI) derivative having four to six isocyanate groups.
2. The adhesive composition of claim 1 , wherein the adhesive composition comprises the first curing agent and the second curing agent in an amount of 0.01 part by weight to 1 part by weight based on 100 parts by weight of the acrylic resin.
3. The adhesive composition of claim 1 , wherein a chain length of the first curing agent is longer than a chain length of the second curing agent.
4. The adhesive composition of claim 1 , wherein the acrylic resin is formed by polymerizing a (meth)acrylic acid ester-based monomer and a hydrophilic functional group-containing monomer.
5. The adhesive composition of claim 4 , wherein the hydrophilic functional group-containing monomer is polymerized in a content of 5 parts by weight to 30 parts by weight based on 100 parts by weight of the (meth)acrylic acid ester-based monomer.
6. The adhesive composition of claim 4 , wherein the hydrophilic functional group-containing monomer is one or more selected from the group consisting of a hydroxyl group-containing monomer, an amino group-containing monomer, a carboxyl group-containing monomer, a sulfone group-containing monomer, a morpholine group-containing monomer, a glycidyl group-containing monomer, and a combination thereof.
7. The adhesive composition of claim 4 , wherein the (meth)acrylic acid ester-based monomer is alkyl (meth)acrylate, and an alkyl of the alkyl(meth)acrylate is a linear or branched C1 to C14 alkyl.
8. The adhesive composition of claim 1 , wherein the acrylic resin has a weight average molecular weight (or a number average molecular weight) of 500,000 to 2,000,000.
9. The adhesive composition of claim 1 , further comprising:
an additive in an amount of 0.5 part by weight to 2 parts by weight based on 100 parts by weight of the acrylic resin.
10. An adhesive film comprising an adhesive layer, which is a cured product of the adhesive composition for touch panels according to claim 1 .
11. The adhesive film of claim 10 , wherein the adhesive layer has a thickness of 10 μm to 50 μm.
12. The adhesive film of claim 10 , wherein the cured product has a gel content of 60% to 90%.
13. A touch panel comprising:
a conductive plastic film which has a conductive layer formed on one side thereof; and
an adhesive layer which is attached to the conductive layer and comprises a cured product of the adhesive composition for touch panels according to claim 1 .
14. The touch panel of claim 13 , wherein the conductive plastic film is a polyethylene terephthalate film having an ITO (conductive metal oxide) layer formed on one side thereof.