Methods To Make Ceramic Proppants
Included are methods to make ceramic proppants. The methods comprise coating green proppants with at least one reactive alumina or zirconium agent, such as gamma alumina. Also included are green proppants and liquid-phase sintered proppants made with the use of the reactive agent. Further included are uses for these proppants, such as in the oil and gas recovery areas.
1 . A method to make ceramic proppants comprising:
coating at least partially a green proppant with at least one reactive agent to form a coated green proppant, wherein said green proppant is a ceramic green proppant that comprises at least aluminosilicate, and
sintering said coated green proppant to form a sintered proppant, wherein said sintering comprises at least liquid-phase sintering, wherein said at least one reactive agent reacts with at least a portion of a glass phase that forms during said sintering.
2 . The method of claim 1 , wherein said reactive agent comprises at least one reactive alumina agent.
3 . The method of claim 1 , wherein said reactive agent comprises at least one reactive zirconium agent.
4 . The method of claim 3 , wherein said reactive zirconium agent is a compound or composition that comprises zirconium oxide, zirconium silicate or both.
5 . The method of claim 2 , wherein said reactive alumina agent comprises less than 95% by weight alpha alumina.
6 . The method of claim 2 , wherein said reactive alumina agent comprises smelter-grade alumina.
7 . The method of claim 2 , wherein said reactive alumina agent comprises at least 10% by weight non-alpha alumina.
8 . The method of claim 2 , wherein said reactive alumina agent is gamma alumina, delta alumina, chi alumina, eta alumina, kappa alumina, or theta alumina, or any combinations thereof.
9 . The method of claim 2 , wherein said reactive alumina agent contains at least 30 wt % of gamma alumina.
10 . The method of claim 1 , wherein said coating is from about 70% to about 100% of the external surface area of the green proppant.
11 . The method of claim 2 , wherein said reactive alumina agent comprises at least one non-alpha hydrated alumina.
12 . The method of claim 2 , wherein said reactive alumina agent has a BET surface area of from about 7 m 2 /g to about 450 m 2 /g.
13 . The method of claim 1 , wherein said reactive agent is present in an amount of from about 0.1 wt % to about 10 wt % based on the weight of said coated green proppant.
14 . The method of claim 1 , wherein said coating has a maximum thickness or an average thickness of from about 1 micron to about 20 microns.
15 . A proppant comprising:
a ceramic green proppant comprising at least aluminosilicate; and
a reactive agent that is at least partially coated on external exposed surface of said ceramic green proppant.
16 . The proppant of claim 15 , wherein the reactive agent is alumina.
17 . The proppant of claim 15 , wherein the reactive agent is zirconium.
18 . A method to make ceramic proppants comprising:
coating at least partially a green proppant with at least one reactive agent to form a coated green proppant, wherein said green proppant is a ceramic green proppant that comprises at least aluminosilicate, and
sintering said coated green proppant to form a sintered proppant, and wherein said sintering comprises at least liquid-phase sintering.
19 . The method of claim 18 , wherein the reactive agent is alumina.
20 . The method of claim 18 , wherein the reactive agent is zirconium.