Manufacturing methods of decorative laminates by inkjet
View Patent ↗A manufacturing method of decorative laminates includes the steps of: a) printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate; b) forming a decorative layer by jetting ink droplets having a volume of up to 30 pL of one or more aqueous pigmented inkjet inks onto the dried ink acceptance layer; and c) heat pressing the decorative layer into a decorative laminate; wherein the ink acceptance layer contains an inorganic pigment P and a polymeric binder B in a weight ratio P/B larger than 1.5.
1. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein
the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the step of heat pressing the decorative layer onto the decorative laminate includes embossing a relief into the decorative laminate.
2. The method according to claim 1 , wherein the paper substrate is impregnated with a thermosetting resin prior to the step of printing the ink acceptance layer.
3. The method according to claim 1 , wherein the droplets forming the ink acceptance layer are jetted using a valve jet print head, a piezoneedle print head, or a through flow print head.
4. The method according to claim 1 , wherein a thickness of the ink acceptance layer varies over a width of the paper substrate by at least 10%.
5. The method according to claim 2 , wherein the thermosetting resin is selected from a group consisting of melamine-formaldehyde based resins, ureum-formaldehyde based resins, and phenol-formaldehyde based resins.
6. The method according to claim 1 , wherein the inorganic pigment P is selected from the group consisting of alumina hydrates, aluminum oxides, aluminum hydroxides, aluminum silicates, and silicas.
7. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein
the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the step of printing the ink acceptance layer includes printing the ink acceptance layer in a single pass inkjet printing mode.
8. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein
the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the step of forming the decorative layer includes jetting the ink droplets in a single pass inkjet printing mode.
9. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein
the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the paper substrate is a bulk colored paper.
10. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the at least one aqueous pigmented inkjet ink includes at least three aqueous pigmented inkjet inks including at least one pigment selected from the group consisting of carbon black, C.I. Pigment Blue 15:3, C.I. Pigment Blue 15:4, C.I Pigment Yellow 150, C.I Pigment Yellow 151, C.I. Pigment Yellow 180, C.I. Pigment Yellow 74, C.I Pigment Red 254, C.I. Pigment Red 176, C.I. Pigment Red 122, and mixed crystals thereof.
11. A manufacturing method of decorative laminates comprising the steps of:
printing an ink acceptance layer by jetting droplets having a volume of 1 to 200 nL onto a paper substrate;
forming a decorative layer by jetting ink droplets having a volume up to 30 pL of at least one aqueous pigmented inkjet ink onto the ink acceptance layer; and
heat pressing the decorative layer onto a decorative laminate; wherein
the ink acceptance layer includes an inorganic pigment P and a polymeric binder B at a weight ratio P/B larger than 1.5; and
the decorative laminate includes a tongue and groove joint that requires no glue.