Splitting of thick hard-foam plates
The present invention relates to a method for cutting rigid foams, especially slabstock P(M)I foams. A method is provided here, by means of which it is possible to cut these rigid foams even in relatively high layer thicknesses of, for example, more than 3 mm, without material loss, which is produced in relevant amounts, for example, in the course of sawing as a result of the sawdust formed.
1. A method for planar division of a rigid foam to obtain a film or thin sheet, said method comprising:
flexibilizing the rigid foam to obtain a flexibilized foam, and
cutting the flexibilized foam with a knife,
wherein said flexibilizing of the rigid foam prior to cutting is accomplished by storing the rigid foam in water and/or heating or adjusting to a temperature in a range of from T-15° C. to T-1° C. where T is a foaming temperature of the rigid foam, and
the rigid foam is a PE, PP, PVC, PMMA or P(M)I foam.
2. The method according to claim 1 , wherein the rigid foam is flexibilized prior to cutting by storing in an oven or by irradiating with IR rays or microwaves.
3. The method according to claim 2 , wherein the rigid foam is cut with the knife directly after removal from an oven or a heated press, or wherein the knife is within the oven.
4. The method according to claim 2 , wherein the rigid foam is first moved past the IR or microwave radiation sources and subsequently transported to the knife with a maximum distance of 2 m, or wherein the radiation source is directly above the knife.
5. The method according to claim 1 , wherein the rigid foam is heated prior to cutting to a temperature above the heat distortion resistance temperature of the rigid foam material.
6. The method according to claim 1 , wherein the rigid foam is stored in a water bath for at least 30 min and then divided with the knife within not more than 30 min.
7. The method according to claim 1 , wherein the rigid foam slab is moved at right angles to the cutting surface of the knife, and wherein the knife moves only at right angles to the transport direction of the rigid foam slab.
8. The method according to claim 1 , wherein the rigid foam is a P(M)I foam having a density between 20 and 320 kg/m 3 .
9. The method according to claim 1 , wherein a film consisting of the rigid foam having a thickness between 0.05 and 1.0 mm is obtained.
10. The method according to claim 1 , wherein a thin sheet consisting of the rigid foam having a thickness between more than 1.0 and a maximum of 30.0 mm is obtained.
11. The method according to claim 1 , wherein the knife is a band knife which moves in a circuit at right angles to the cutting direction.
12. The method according to claim 9 , wherein the film or the thin sheet is subsequently covered with at least one outer layer.
13. The method according to claim 1 , wherein several films or thin sheets are divided off from the rigid foam after the flexibilizing, in one movement with several knives in succession.
14. The method according to claim 1 , wherein the film or thin sheet is divided off, and after having been divided, is cut to size in the two other dimensions.
15. The method according to claim 9 , wherein the film divided off is subsequently wound onto a roll.