Laser-markable and laser-weldable polymeric materials
The present invention relates to colored laser-markable and laser-weldable polymeric materials which are distinguished by the fact that they comprise, as absorber, at least one doped tin oxide or indium oxide having a large specific surface area.
1. A laser-markable and/or laser-weldable polymer composition, said polymer composition comprising:
a polymer, at least one colorant and, as an absorber, a doped tin oxide or indium oxide having a specific surface area of at least 15 m 2 /g,
wherein said absorber is in the form of porous aggregates of primary particles, and said at least one colorant is selected from organic pigments and dyes.
2. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein said absorber is at least one fluorine-doped tin oxide, antimony-doped tin oxide, or indium tin oxide.
3. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein said absorber is a doped tin oxide in which the content of dopants is 1-15 mol %, based on the tin oxide.
4. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the porous aggregates of absorber have a number average particle size of <5 μm, measured at the D 90 by means of laser diffraction.
5. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the primary particles have a diameter of less than 100 nm.
6. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein said absorber is employed in a concentration of 0.005 to 1% by weight, based on the polymer.
7. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the polymer is a thermoplastic, thermoset or elastomer.
8. A process for preparation of laser-markable and/or laser-weldable polymer compositions according to claim 1 , said process comprising
adding the absorber simultaneously or successively by compounding, via a masterbatch or via pastes or by direct addition to the polymer,
optionally adding one or more additives, and
shaping the polymer under the action of heat.
9. A method for imaging, comprising marking a laser-markable and/or laser-weldable polymer compositions according to claim 1 .
10. A molding composition, semi-finished product, or finished part comprising a laser-markable and laser-weldable polymer composition according to claim 1 .
11. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the absorber has a specific surface area of at least 20 m 2 /g.
12. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the absorber has a specific surface area of at least 25 m 2 /g.
13. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the absorber has a weight average particle size of ≤10 μm, measured at the D 90 by means of laser diffraction.
14. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the absorber has a weight average particle size of ≤2 μm, measured at the D 90 by means of laser diffraction.
15. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein the primary particles have a diameter of less than 50 nm.
16. The laser-markable and/or laser-weldable polymer composition according to claim 6 , wherein said absorber is employed in a concentration of 0.05-0.5% by weight, based on the polymer.
17. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein said absorber is a support-free antimony-doped tin oxide or a fluoride-doped tin oxide, wherein the content of dopants in the tin oxide is 1-15 mol %.
18. The laser-markable and/or laser-weldable polymer composition according to claim 1 , wherein said absorber is a support-free antimony-doped tin oxide or a fluoride-doped tin oxide, wherein the content of dopants in the tin oxide is 3-10 mol %.