High-strength crystallized glass ceramic comprising wollastonite, hydroxyapatite and akermanite
The present invention relates to a crystallized glass ceramic comprising 30 wt % to 40 wt % of each of CaSiO 3 , Ca 10 (PO 4 ) 6 (OH) 2 , and Ca 2 Mg(Si 2 O 7 ); a crystallized glass ceramic composition comprising CaSiO 3 , Ca 10 (PO 4 ) 6 (OH) 2 , and Ca 2 Mg(Si 2 O 7 ) in a predetermined weight ratio; a bone graft material comprising the glass ceramic; and an intervertebral spacer or medical device for replacement of bone tissue, which is manufactured using the bone graft material.
1. A crystallized glass ceramic comprising CaSiO 3 , Ca 10 (PO 4 ) 6 (OH) 2 , and Ca 2 Mg(Si 2 O 7 ) at a weight ratio of 30 to 40:30 to 40:30 to 40.
2. The crystallized glass ceramic of claim 1 , wherein CaSiO3 comprises a wollastonite, Ca 10 (PO 4 ) 6 (OH) 2 comprises a hydroxyapatite (HA), and Ca 2 Mg(Si 2 O 7 ) comprises an akermanite.
3. The crystallized glass ceramic of claim 1 , wherein the crystallized glass ceramic has increased compressive strength or flexural strength compared to glass ceramics comprising CaSiO 3 and Ca 10 (PO 4 ) 6 (OH) 2 due to Ca 2 Mg(Si 2 O 7 ).
4. The crystallized glass ceramic of claim 1 , wherein the crystallized glass ceramic is formed by sintering at a temperature of about 850° C. to about 1,100° C.
5. The crystallized glass ceramic of claim 1 , which is manufactured by sintering a glass ceramic composition, wherein the glass ceramic composition is manufactured by a process comprising boiling a raw composition comprising SiO 2 , hydroxyapatite, Ca(OH) 2 , MgO, CaF 2 , and B 2 O 3 ,
wherein the raw composition comprises SiO 2 hydroxyapatite, Ca(OH) 2 , MgO, CaF 2 at a weight ratio of 25 to 35:25 to 35:18 to 22:4 to 6:4 to 5.
6. A bone graft material comprising the glass ceramic according to claim 1 .
7. An intervertebral spacer or medical device for replacement of bone tissue: manufactured using the bone graft material of claim 6 ; or, comprising the bone graft material of claim 6 .
8. The intervertebral spacer or medical device of claim 7 , wherein the intervertebral spacer or medical device has compressive strength in a range of about 3,000 N to about 35,000 N or the torsional strength in a range of about 0.6 Nm to about 1.5 Nm.
9. The intervertebral spacer or medical device of claim 7 , wherein the intervertebral spacer or medical device is manufactured using a bone graft material, wherein the bone graft material comprises a dense molded product having a value of relative density corresponding to about 95% or higher relative to that of theoretical density.