Austenitic-based stainless steel for molten carbonate fuel cell
Provided is an austenitic stainless steel for a fuel cell including, in weight %, C: 0.05% to 0.09%, Si: 0.5% or less (0 excluded), Mn: 2.5% to 5.0%, Cr: 21% to 23%, Ni: 10% to 12%, Nb: 0.2% to 0.7%, N: 0.25% or less (0 excluded), Al: 0.2% or less (0 excluded), S: 0.003% or less (0 excluded), B: 0.01% or less (0 excluded), the remainder being Fe and unavoidable impurities.
1. Austenitic stainless steel for a molten carbonate fuel cell comprising, in weight %, C: 0.05% to 0.09%, Si: 0.5% or less (0 excluded), Mn: 2.5% to 5.0%, Cr: 21% to 23%, Ni: 10% to 12%, Nb: 0.2% to 0.7%, N: 0.25% or less (0 excluded), Al: 0.2% or less (0 excluded), S: 0.003% or less (0 excluded), B: 0.01% or less (0 excluded), the remainder being Fe and unavoidable impurities, and
a scale formed on a surface of the austenitic stainless steel, the scale having a contact resistance of 80 mΩ*cm 2 or less.
2. The austenitic stainless steel for a molten carbonate fuel cell of claim 1 , wherein the scale includes Cr oxide and Mn oxide.
3. The austenitic stainless steel for a molten carbonate fuel cell of claim 2 , wherein the Cr oxide includes a Cr—Mn—O spinel phase, and the Mn oxide includes a Cr—Mn—O spinel phase and an Fe—Mn—O spinel phase.
4. The austenitic stainless steel for a molten carbonate fuel cell of claim 2 , wherein Nb is doped to the Mn oxide.
5. The austenitic stainless steel for a molten carbonate fuel cell of claim 3 , wherein Nb is doped to the Mn oxide.