Polypropylene with enhanced visual appearance

1. Polymer composition, comprising:

(i) polypropylene (PP),

(ii) 0.03 to 0.2 wt % of a first nucleating agent (NU1) which is 1,3:2,4 bis(3,4-dimethylbenzylidene)sorbitol, and

(iii) 0.04 to 0.06 wt % of a zinc fatty acid salt,

wherein the first nucleating agent (NU1) and the zinc fatty acid salt, together fulfill the inequality (If):

5

≥

W

⁡

(

NU

1

)

W

⁡

(

EAF

)

≥

0.5

(

If

)

wherein “W (NU1)” is the weight [wt %] of the first nucleating agent (NU1), based on the weight of the polymer composition and “W (EAF)” is the weight [wt %] of the zinc fatty acid salt, based on the weight of the polymer composition; and wherein the polymer composition comprises an optical brightener (OB), the optical brightener is selected from the group consisting of 5-methyl-2,2′-(vinylenedi-p-phenylene)bis-benzoxazole, 2,2′-(4,4′-diphenol vinyl)dibenzoxazole, 2,5-bis(5-tert-butylbenzooxazol-2-yl)thiophene, 1,4-bis(2-benzoxazolyl)naphthalene, and 2-(5-chlorobenzo[d]oxazol-2-yl)acetonitrile.

2. Polymer composition according to claim 1 , wherein the polymer composition:

(a) does not contain calcium stearate, and/or

(b) comprises a second nucleating agent (NU2).

3. Polymer composition according to claim 1 comprising:

(i) the polypropylene (PP) in an amount of more than 95.0 wt % based on the weight of the polymer composition,

(iv) optionally a second nucleating agent (NU2) in an amount of equal or below 1.0 wt %, based on the weight of the polymer composition, and

(v) the optical brightener (OB) in an amount of equal or below 0.100 wt %, based on the weight of the polymer composition.

4. Polymer composition according to claim 1 , wherein the polypropylene (PP):

(a) is a propylene copolymer comprising equal to or below 5 wt % comonomer, wherein the comonomer is selected from ethylene and/or one or more C 4 -C 8 α-olefins, and/or

(b) is monophasic.

5. Polymer composition according to claim 1 , further comprising alkali earth fatty acid salt, wherein the weight ratio between the zinc fatty acid salt, and the alkali earth fatty acid salt, is 20/80 to 80/20.

6. Polymer composition according to claim 3 , obtained from melt-blending at a temperature in the range of 110 to 140° C., the polypropylene (PP) with the first nucleating agent (NU1), the zinc fatty acid salt, optionally an alkali earth fatty acid salt, optionally the second nucleating agent (NU2) and the optical brightener (OB).

7. Polymer composition according to claim 1 , having:

(a) a haze in the range from 20 to 40%, wherein the haze is measured according to ASTM D 1003-07 on 60×60 mm 2 plaques thickness of 2 mm prepared according to EN ISO 1873-2 at a processing temperature of the plaques of 190° C., and/or

(b) yellowness index in the range of −20 to 15, as determined according to ASTM E313.

8. Molded article comprising a polymer composition according to claim 1 .

9. Molded article according to claim 8 , wherein the article is an injection molded article, blow molded article, a co-injection-gas assisted molding article, a structural foam molding article, an extrusion blow molding article, an injection blow molding article or an injection stretch molding article.

10. Molded article according to claim 8 , wherein the article has a thickness from 0.3 to 5.0 mm.